| Manufacturer | Prime Polymer Co., Ltd. |
| Resin Name | C4-LLDPE |
| Product Name | Neozex |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183 | Density | ISO1183 | g/cm^3 | 0.92 | - |
Density | JISK7112 | g/cm^3 | 0.92 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO306 | Vicat softening point | ISO306 | ℃ | 100 | - |
Vicat softening point | JISK7206 | ℃ | 100 | - | |
Melting point Melting point/ISO11357-3 | Melting point | ISO11357-3 | ℃ | 120 | - |
Melting point | JISK7121 | ℃ | 120 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile strain at break Tensile strain at break/ISO527-1,2 | Nominal tensile strain at break | ISO527-1,2 | % | 370 | - |
Nominal tensile strain at break | JISK7161,JISK7162 | % | 370 | - | |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus | ISO178 | MPa | 200 | - |
Flexural modulus | JISK7171 | MPa | 200 | - | |
Charpy impact strength Charpy impact strength/ISO179-1 | Charpy impact strength | ISO179-1 | kJ/m^2 | NB | |
Charpy impact strength | JISK7111 | kJ/m^2 | NB |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
ＭＦＲ ＭＦＲ/ISO1133 | Melt Mass Flow Rate | ISO1133 | g/10min | 0.6 | - |
Melt Mass Flow Rate | JISK7210 | g/10min | 0.6 | - |
| Main Applications |
|---|
Tube, Soft Bottle |
| Key Features |
|---|
Formability, generally used |