| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Resin Name | PC |
| Product Name | Toughlon |
| ISO Material Code | >PC-GF20< |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183 | Density | ISO1183 | g/cm^3 | 1.32 | - |
Density | JISK7112 | g/cm^3 | 1.32 | - | |
Water absorption Water absorption/ISO62 | Water absorption (24h, 50%RH) | ISO62 | % | 0.09 | - |
Water absorption (24h, 50%RH) | JISK7209 | % | 0.09 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75-1,ISO75-2 | Deflection temperature under load (1.8MPa) | ISO75-1,ISO75-2 | ℃ | 144 | - |
Deflection temperature under load (0.45MPa) | ISO75-1,ISO75-2 | ℃ | 148 | - | |
Deflection temperature under load (1.8MPa) | JISK7191-1,JISK7191-2 | ℃ | 144 | - | |
Deflection temperature under load (0.45MPa) | JISK7191-1,JISK7191-2 | ℃ | 148 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile strain at break Tensile strain at break/ISO527-1,ISO527-2 | Tensile strain at break | ISO527-1,ISO527-2 | % | 3 | - |
Tensile strain at break | JISK7161,JISK7162 | % | 3 | - | |
Bending strength Bending strength/ISO178 | Bending strength | ISO178 | Mpa | 150 | - |
Bending strength | JISK7171 | Mpa | 150 | - | |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus | ISO178 | Mpa | 5300 | - |
Flexural modulus | JISK7171 | Mpa | 5300 | - | |
Charpy impact strength Charpy impact strength/ISO179-1 | Charpy impact strength (notched, 23℃) | ISO179-1 | kJ/m^2 | 22 | - |
Charpy impact strength (notched, 0℃) | ISO179-1 | kJ/m^2 | 18 | - | |
Charpy impact strength (notched, -30℃) | ISO179-1 | kJ/m^2 | 18 | - | |
Charpy impact strength (notched, 23℃) | JISK7111 | kJ/m^2 | 22 | - | |
Charpy impact strength (notched, 0℃) | JISK7111 | kJ/m^2 | 18 | - | |
Charpy impact strength (notched, -30℃) | JISK7111 | kJ/m^2 | 18 | - | |
Izod impact strength Izod impact strength/ASTMD256 | Izod impact strength (notched, 23℃) | ASTMD256 | J/m | 190 | - |
Izod impact strength (notched, -30℃) | ASTMD256 | J/m | 170 | - | |
Surface hardness Surface hardness/ISO2039-2 | Rockwell hardness | ISO2039-2 | R scale | 120 | - |
Rockwell hardness | ISO2039-2 | M scale | 70 | - | |
Rockwell hardness | JISK7202-2 | R scale | 120 | - | |
Rockwell hardness | JISK7202-2 | M scale | 70 | - | |
Tensile strength Tensile strength/JISK7161,JISK7162 | Tensile (yield) strength | JISK7161,JISK7162 | Mpa | 105 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/Idemitsu Method | Mold shrinkage rate (2mm,MD) | Idemitsu Method | % | 0.38 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/Idemitsu Method | Mold shrinkage rate (2mm,TD) | Idemitsu Method | % | 0.51 | - |
MVR MVR/ISO1133 | Melt volume flow rate (MVR, 300℃, 1.20kg) | ISO1133 | cm^3/10min | 6 | - |
Melt volume flow rate (MVR, 300℃, 1.20kg) | JISK7210 | cm^3/10min | 6 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - |
| Key Features |
|---|
Siloxane PC copolymer, GF reinforced, impact resistant |