| Manufacturer | Ube Maruzen Polyethylene Co., Ltd. |
| Resin Name | LDPE |
| Product Name | Ube Polyethylene |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/JIS-K7112 | Density | JIS-K7112 | g/cm3 | 0.928 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/JIS-K7113 | Tensile breaking stress | JIS-K7113 | MPa | 16 | - |
Tensile strain at break Tensile strain at break/JIS-K7113 | Tensile strain at break | JIS-K7113 | % | 550 | - |
Flexural modulus Flexural modulus/JIS-K7171 | Flexural modulus | JIS-K7171 | MPa | 380 | - |
Surface hardness Surface hardness/JIS-K7215 | Durometer | JIS-K7215 | D | 57 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Volume resistivity Volume resistivity/ASTM-D257 | Volume resistivity | ASTM-D257 | NaN | - | |
Dielectric constant Dielectric constant/- | Dielectric constant | - | 2.3 | - | |
Dielectric loss tangent Dielectric loss tangent/ASTM-D1531 | Dielectric loss tangent | ASTM-D1531 | 0.0001 | - | |
Insulation strength Insulation strength/ASTM-D149 | Insulation strength | ASTM-D149 | 36 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
MFR MFR/JIS-K7210 | MFR | JIS-K7210 | g/10min | 0.9 | - |
| Main Applications |
|---|
Silane crosslinking base |
| Key Features |
|---|
Processability, heat resistance |