| Manufacturer | Ube Maruzen Polyethylene Co., Ltd. |
| Resin Name | LDPE |
| Product Name | Ube Polyethylene |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/JIS-K7112 | Density | JIS-K7112 | g/cm3 | 0.922 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/JIS-K7206 | Vicat softening temperature | JIS-K7206 | ℃ | 90 | - |
Melting point Melting point/UBE method | Melting point | UBE method | ℃ | 110 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/JIS-K7113 | Tensile breaking stress | JIS-K7113 | MPa | 14 | - |
Tensile strain at break Tensile strain at break/JIS-K7113 | Tensile strain at break | JIS-K7113 | % | 550 | - |
Flexural modulus Flexural modulus/JIS-K7171 | Flexural modulus | JIS-K7171 | MPa | 240 | - |
Surface hardness Surface hardness/JIS-K7215 | Durometer | JIS-K7215 | D | 52 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
MFR MFR/JIS-K7210 | MFR | JIS-K7210 | g/10min | 5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
- | 145 | - |
| Main Applications |
|---|
Thin Film |
| Key Features |
|---|
Ductility |