| Manufacturer | Celanese Corporation |
| Resin Name | PA66 |
| Product Name | Zytel |
| ISO Material Code | PA66 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (dry) | ISO 1183 | g/cm^3 | 1.14 | - |
Water absorption Water absorption/ISO 62 | Equilibrium water absorption (2mm) (when absorbing moisture) | ISO 62 | % | 2.6 | - |
Water absorption (immersion, 24h) (when completely dry) | ISO 62 | % | 1.2 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1/-2 | Deflection temperature under load (1.80 MPa) (when completely dry) | ISO 75-1/-2 | ℃ | 70 | - |
Deflection temperature under load (0.45 MPa) (when completely dry) | ISO 75-1/-2 | ℃ | 200 | - | |
Melting point Melting point/ISO 11357-1/-3 | Melting temperature (10℃/min) (when completely dry) | ISO 11357-1/-3 | ℃ | 262 | - |
Flammability Flammability/IEC 60695-11-10 | Flammability | IEC 60695-11-10 | class | NaN | 1.5ｍｍ |
Glass transition temperature Glass transition temperature/ISO 11357-1/-3 | Glass transition temperature (10℃/min) (when completely dry) | ISO 11357-1/-3 | ℃ | 60 | - |
Glass transition temperature (10℃/min) (at 23℃ 50% RH equilibrium water absorption) | ISO 11357-1/-3 | ℃ | 40 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527-1/-2 | Yield stress (absolutely dry) | ISO 527-1/-2 | MPa | 85 | - |
Yield stress (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | MPa | 55 | - | |
Tensile strain at break Tensile strain at break/ISO 527-1/-2 | Nominal breaking strain (when completely dry) | ISO 527-1/-2 | % | 20 | - |
Nominal strain at break (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | % | 50 | - | |
Tensile Modulus Tensile Modulus/ISO 527-1/-2 | Tensile modulus (when completely dry) | ISO 527-1/-2 | MPa | 3100 | - |
Tensile modulus (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | MPa | 1400 | - | |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus (when completely dry) | ISO 178 | MPa | 2800 | - |
Flexural modulus (at 23℃ 50% RH equilibrium water absorption) | ISO 178 | MPa | 1300 | - | |
Charpy impact strength Charpy impact strength/ISO 179/1eA | Notched Charpy impact strength (23°C) (when completely dry) | ISO 179/1eA | kJ/m^2 | 5.5 | - |
Notched Charpy impact strength (23℃) (23℃ 50%RH equilibrium water absorption) | ISO 179/1eA | kJ/m^2 | 12 | - | |
Notched Charpy impact strength (-30℃) (absolutely dry) | ISO 179/1eA | kJ/m^2 | 3 | - | |
Notched Charpy impact strength (-30℃) (23℃ 50%RH equilibrium water absorption) | ISO 179/1eA | kJ/m^2 | 3 | - | |
Notched Charpy impact strength (-40℃) (absolutely dry) | ISO 179/1eA | kJ/m^2 | 2.5 | - | |
Notched Charpy impact strength (-40℃) (23℃ 50%RH equilibrium water absorption) | ISO 179/1eA | kJ/m^2 | 2.5 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength, notched (23°C) (when completely dry) | ISO 180/1A | kJ/m^2 | 5 | - |
Izod impact strength, notched (23°C) (at 23°C, 50% RH, equilibrium water absorption) | ISO 180/1A | kJ/m^2 | 11 | - | |
Izod impact strength, notched (-40°C) (absolutely dry) | ISO 180/1A | kJ/m^2 | 5 | - | |
Izod impact strength, notched (-40℃) (23℃ 50% RH equilibrium water absorption) | ISO 180/1A | kJ/m^2 | 4 | - | |
Yield Strain Yield Strain/ISO 527-1/-2 | Yield strain (when completely dry) | ISO 527-1/-2 | % | 4.3 | - |
Yield strain (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | % | 25 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tracking resistance Tracking resistance/IEC 60112 | Tracking resistance (when completely dry) | IEC 60112 | 600 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294-4,2577 | Mold shrinkage rate (parallel) (when completely dry) | ISO 294-4,2577 | % | 1.3 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 294-4,2577 | Mold shrinkage rate (vertical) (when completely dry) | ISO 294-4,2577 | % | 1.3 | - |
MFR MFR/ISO 1133 | Melt mass flow rate (275℃, 2.16kg) (when completely dry) | ISO 1133 | g/10min | 36 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/- | Optimum resin temperature | - | ℃ | 290 | - |
Mold Temperature Mold Temperature/- | Optimal Mold Temperature | - | ℃ | 70 | - |
Drying conditions Drying conditions/- | Drying temperature | - | ℃ | 80 | 2 - 4h |
| Key Features |
|---|
Non-reinforced, heat-resistant |