| Manufacturer | Celanese Corporation |
| Resin Name | PA66 |
| Product Name | Zytel |
| ISO Material Code | PA66-I |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (dry) | ISO 1183 | g/cm^3 | 1.1 | - |
Water absorption Water absorption/ISO 62 | Water absorption (immersion, 24h) (when completely dry) | ISO 62 | % | 1.2 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1/-2 | Deflection temperature under load (1.80 MPa) (when completely dry) | ISO 75-1/-2 | ℃ | 63 | - |
Deflection temperature under load (0.45 MPa) (when completely dry) | ISO 75-1/-2 | ℃ | 102 | - | |
Melting point Melting point/ISO 11357-1/-3 | Melting temperature (10℃/min) (when completely dry) | ISO 11357-1/-3 | ℃ | 263 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527-1/-2 | Yield stress (absolutely dry) | ISO 527-1/-2 | MPa | 61 | - |
Yield stress (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | MPa | 46 | - | |
Tensile strain at break Tensile strain at break/ISO 527-1/-2 | Breaking strain (when completely dry) | ISO 527-1/-2 | % | 37 | - |
Breaking strain (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | % | 118 | - | |
Nominal breaking strain (when completely dry) | ISO 527-1/-2 | % | 20 | - | |
Nominal strain at break (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | % | 50 | - | |
Tensile Modulus Tensile Modulus/ISO 527-1/-2 | Tensile modulus (when completely dry) | ISO 527-1/-2 | MPa | 2500 | - |
Tensile modulus (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | MPa | 1200 | - | |
Charpy impact strength Charpy impact strength/ISO 179/1eA | Notched Charpy impact strength (23°C) (when completely dry) | ISO 179/1eA | kJ/m^2 | 16 | - |
Notched Charpy impact strength (23℃) (23℃ 50%RH equilibrium water absorption) | ISO 179/1eA | kJ/m^2 | 20 | - | |
Notched Charpy impact strength (-30℃) (absolutely dry) | ISO 179/1eA | kJ/m^2 | 9 | - | |
Notched Charpy impact strength (-30℃) (23℃ 50%RH equilibrium water absorption) | ISO 179/1eA | kJ/m^2 | 5 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength, notched (23°C) (when completely dry) | ISO 180/1A | kJ/m^2 | 15 | - |
Izod impact strength, notched (23°C) (at 23°C, 50% RH, equilibrium water absorption) | ISO 180/1A | kJ/m^2 | 18 | - | |
Izod impact strength, notched (-30°C) (absolutely dry) | ISO 180/1A | kJ/m^2 | 9 | - | |
Izod impact strength, notched (-30℃) (23℃ 50% RH equilibrium water absorption) | ISO 180/1A | kJ/m^2 | 6 | - | |
Izod impact strength, notched (-40°C) (absolutely dry) | ISO 180/1A | kJ/m^2 | 11 | - | |
Izod impact strength, notched (-40℃) (23℃ 50% RH equilibrium water absorption) | ISO 180/1A | kJ/m^2 | 7 | - | |
Yield Strain Yield Strain/ISO 527-1/-2 | Yield strain (when completely dry) | ISO 527-1/-2 | % | 6 | - |
Yield strain (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | % | 25 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/- | Optimum resin temperature | - | ℃ | 290 | - |
Mold Temperature Mold Temperature/- | Optimal Mold Temperature | - | ℃ | 70 | - |
Drying conditions Drying conditions/- | Drying temperature | - | ℃ | 80 | 2 - 4h |
| Key Features |
|---|
Unreinforced, impact and heat resistant |