Density (dry)

ISO 1183

g/cm^3

-

Equilibrium water absorption (2mm) (when absorbing moisture)

ISO 62

%

-

Water absorption (immersion, 24h) (when completely dry)

ISO 62

%

-

Deflection temperature under load (1.80 MPa) (when completely dry)

ISO 75-1/-2

℃

-

Deflection temperature under load (0.45 MPa) (when completely dry)

ISO 75-1/-2

℃

-

Linear expansion coefficient (parallel) (when completely dry)

ISO 11359-1/-2

x10^-5/℃

-

Linear expansion coefficient (right angle) (when completely dry)

ISO 11359-1/-2

x10^-5/℃

-

Melting temperature (10℃/min) (when completely dry)

ISO 11357-1/-3

℃

-

Flammability

IEC 60695-11-10

class

1.5ｍｍ

Glass transition temperature (10℃/min) (when completely dry)

ISO 11357-1/-3

℃

-

Glass transition temperature (10℃/min) (at 23℃ 50% RH equilibrium water absorption)

ISO 11357-1/-3

℃

-

Breaking stress (when completely dry)

ISO 527-1/-2

MPa

-

Breaking stress (at 23℃ 50% RH equilibrium water absorption)

ISO 527-1/-2

MPa

-

Breaking strain (when completely dry)

ISO 527-1/-2

%

-

Breaking strain (at 23℃ 50% RH equilibrium water absorption)

ISO 527-1/-2

%

-

Tensile modulus (when completely dry)

ISO 527-1/-2

MPa

-

Tensile modulus (at 23℃ 50% RH equilibrium water absorption)

ISO 527-1/-2

MPa

-

Bending strength (when completely dry)

ISO 178

MPa

-

Bending strength (at 23℃ 50% RH equilibrium water absorption)

ISO 178

MPa

-

Flexural modulus (when completely dry)

ISO 178

MPa

-

Flexural modulus (at 23℃ 50% RH equilibrium water absorption)

ISO 178

MPa

-

Notched Charpy impact strength (23°C) (when completely dry)

ISO 179/1eA

kJ/m^2

-

Notched Charpy impact strength (23℃) (23℃ 50%RH equilibrium water absorption)

ISO 179/1eA

kJ/m^2

-

Notched Charpy impact strength (-30℃) (23℃ 50%RH equilibrium water absorption)

ISO 179/1eA

kJ/m^2

-

Notched Charpy impact strength (-40℃) (absolutely dry)

ISO 179/1eA

kJ/m^2

-

Charpy impact strength (23℃) (when completely dry)

ISO 179/1eU

kJ/m^2

-

Charpy impact strength (23℃) (23℃ 50% RH equilibrium water absorption)

ISO 179/1eU

kJ/m^2

-

Charpy impact strength (-30℃) (when completely dry)

ISO 179/1eU

kJ/m^2

-

Charpy impact strength (-30℃) (23℃ 50% RH equilibrium water absorption)

ISO 179/1eU

kJ/m^2

-

Izod impact strength, notched (23°C) (when completely dry)

ISO 180/1A

kJ/m^2

-

Izod impact strength, notched (23°C) (at 23°C, 50% RH, equilibrium water absorption)

ISO 180/1A

kJ/m^2

-

Izod impact strength, notched (-30°C) (absolutely dry)

ISO 180/1A

kJ/m^2

-

Izod impact strength, notched (-30℃) (23℃ 50% RH equilibrium water absorption)

ISO 180/1A

kJ/m^2

-

Izod impact strength, notched (-40°C) (absolutely dry)

ISO 180/1A

kJ/m^2

-

Izod impact strength, notched (-40℃) (23℃ 50% RH equilibrium water absorption)

ISO 180/1A

kJ/m^2

-

Izod impact strength, unnotched (23°C) (when completely dry)

ISO 180/1U

kJ/m^2

-

Izod impact strength, unnotched (23°C) (at 23°C and 50% RH when absorbing water at equilibrium)

ISO 180/1U

kJ/m^2

-

Izod impact strength, unnotched (-30°C) (when completely dry)

ISO 180/1U

kJ/m^2

-

Izod impact strength, unnotched (-30℃) (23℃ 50% RH equilibrium water absorption)

ISO 180/1U

kJ/m^2

-

Volume resistivity (when completely dry)

IEC 62631-3-1

Ω・cm

-

Dielectric loss tangent, 100Hz (when completely dry)

IEC 62631-2-1

E-4

-

Dielectric tangent, 100Hz (23℃ 50%RH equilibrium water absorption)

IEC 62631-2-1

E-4

-

Dielectric tangent, 1MHz (when completely dry)

IEC 62631-2-1

E-4

-

Dielectric tangent, 1MHz (23℃ 50%RH equilibrium water absorption)

IEC 62631-2-1

E-4

-

Mold shrinkage rate (parallel) (when completely dry)

ISO 294-4,2577

%

-

Mold shrinkage rate (vertical) (when completely dry)

ISO 294-4,2577

%

-

Optimum resin temperature

-

℃

-

Optimal Mold Temperature

-

℃

-

Drying temperature

-

℃

2 - 4h

Filler Content

%

GF