| Manufacturer | Celanese Corporation |
| Resin Name | PA66+PA6 |
| Product Name | Zytel |
| ISO Material Code | (PA66+PA6)-GF33 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (dry) | ISO 1183 | g/cm^3 | 1.39 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1/-2 | Deflection temperature under load (1.80 MPa) (when completely dry) | ISO 75-1/-2 | ℃ | 225 | - |
Melting point Melting point/ISO 11357-1/-3 | Melting temperature (10℃/min) (when completely dry) | ISO 11357-1/-3 | ℃ | 245 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO 527-1/-2 | Breaking stress (when completely dry) | ISO 527-1/-2 | MPa | 194 | - |
Breaking stress (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | MPa | 130 | - | |
Tensile strain at break Tensile strain at break/ISO 527-1/-2 | Breaking strain (when completely dry) | ISO 527-1/-2 | % | 4 | - |
Breaking strain (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | % | 6 | - | |
Tensile Modulus Tensile Modulus/ISO 527-1/-2 | Tensile modulus (when completely dry) | ISO 527-1/-2 | MPa | 10900 | - |
Tensile modulus (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | MPa | 7500 | - | |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus (when completely dry) | ISO 178 | MPa | 8900 | - |
Charpy impact strength Charpy impact strength/ISO 179/1eA | Notched Charpy impact strength (23°C) (when completely dry) | ISO 179/1eA | kJ/m^2 | 16 | - |
Notched Charpy impact strength (23℃) (23℃ 50%RH equilibrium water absorption) | ISO 179/1eA | kJ/m^2 | 18 | - | |
Notched Charpy impact strength (-30℃) (absolutely dry) | ISO 179/1eA | kJ/m^2 | 10 | - | |
Notched Charpy impact strength (-30℃) (23℃ 50%RH equilibrium water absorption) | ISO 179/1eA | kJ/m^2 | 10 | - | |
Notched Charpy impact strength (-40℃) (absolutely dry) | ISO 179/1eA | kJ/m^2 | 12.3 | - | |
Charpy impact strength (23℃) (when completely dry) | ISO 179/1eU | kJ/m^2 | 95 | - | |
Charpy impact strength (23℃) (23℃ 50% RH equilibrium water absorption) | ISO 179/1eU | kJ/m^2 | 100 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294-4,2577 | Mold shrinkage rate (parallel) (when completely dry) | ISO 294-4,2577 | % | 0.3 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 294-4,2577 | Mold shrinkage rate (vertical) (when completely dry) | ISO 294-4,2577 | % | 0.9 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/- | Optimum resin temperature | - | ℃ | 290 | - |
Mold Temperature Mold Temperature/- | Optimal Mold Temperature | - | ℃ | 100 | - |
Drying conditions Drying conditions/- | Drying temperature | - | ℃ | 80 | 2 - 4h |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 33 | GF |
| Key Features |
|---|
Weather resistance |