| Manufacturer | Dow Mitsui Polychemicals Co., Ltd. |
| Resin Name | Special Resin |
| Product Name | Nuclell |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/JIS K7112:1999 | Density | JIS K7112:1999 | g/cm^3 | 0.94 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/JIS K7206:1999 | Vicat softening temperature | JIS K7206:1999 | ℃ | 78 | - |
Melting point Melting point/DSC | Melting point | DSC | ℃ | 98 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/JIS K7161-1:2014,JIS K7161-2:2014 | Tensile breaking stress | JIS K7161-1:2014,JIS K7161-2:2014 | MPa | 26 | - |
Tensile strain at break Tensile strain at break/JIS K7161-1:2014,JIS K7161-2:2014 | Tensile strain at break | JIS K7161-1:2014,JIS K7161-2:2014 | % | 500 | - |
Flexural modulus Flexural modulus/JIS K7106:1995 | Bending rigidity | JIS K7106:1995 | MPa | 140 | - |
Surface hardness Surface hardness/JIS K7215:1986 | Durometer D Hardness | JIS K7215:1986 | 54 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
ＭＦＲ ＭＦＲ/JIS K7210:1999 | Melt mass flow rate (190℃/2.16kg load) | JIS K7210:1999 | g/10min | 8 | - |
| Key Features |
|---|
EMAA |