| Manufacturer | Toray Celanese Co., Ltd. |
| Resin Name | TPE |
| Product Name | Hytrel |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Proportion | ASTM D792 | 1.15 | - | |
Water absorption Water absorption/ASTM D570 | Water absorption (23℃, 24H) | ASTM D570 | % | 0.8 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/JIS K7206 | Vicat softening temperature (A method) | JIS K7206 | ℃ | 111 | - |
Deflection Temperature under Load Deflection Temperature under Load/ASTM D648 | Deflection temperature under load (0.45MPa) | ASTM D648 | ℃ | 59 | - |
Melting point Melting point/DSC | Melting point | DSC | ℃ | 163 | - |
Flammability Flammability/UL 94 | Flammability | UL 94 | NaN | - | |
Glass transition Glass transition/DSC | Glass transition temperature | DSC | ℃ | -26 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/JIS K7113-1995 | Tensile Yield Strength | JIS K7113-1995 | MPa | 6.9 | - |
Tensile breaking stress Tensile breaking stress/JIS K7113-1995 | Tensile breaking stress | JIS K7113-1995 | MPa | 21.2 | - |
Tensile strain at break Tensile strain at break/JIS K7113-1995 | Tensile elongation at break | JIS K7113-1995 | % | 607 | - |
Tensile Modulus Tensile Modulus/JIS K7113-1995 | Tensile Modulus | JIS K7113-1995 | MPa | 32.3 | - |
Bending strength Bending strength/ASTM D790 | Bending strength | ASTM D790 | MPa | 3.5 | - |
Flexural modulus Flexural modulus/ASTM D790 | Flexural modulus | ASTM D790 | MPa | 53.4 | - |
Tear strength Tear strength/ASTM D624 | Tear strength (die C, 2mmt) | ASTM D624 | kN/m | 100 | - |
Izod impact strength Izod impact strength/ASTM D256 | Izod impact strength (23°C, notched) | ASTM D256 | J/m | NB | |
Izod impact strength (-20℃, notched) | ASTM D256 | J/m | NB | ||
Surface hardness Surface hardness/JIS K7215 | Surface hardness (durometer) | JIS K7215 | D Scale | 40 | - |
Surface hardness (durometer) | JIS K7215 | A Scale | 90 | - | |
Tensile strength Tensile strength/JIS K7113-1995 | 10% tensile strength | JIS K7113-1995 | MPa | 3.2 | - |
Tensile elongation Tensile elongation/JIS K7113-1995 | Tensile Yield Elongation | JIS K7113-1995 | % | -50 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Volume resistivity Volume resistivity/ASTM D257 | Volume resistance (23℃, 51%RH) | ASTM D257 | Ω・cm | NaN | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage Mold shrinkage/ | Molding shrinkage rate (tensile test piece 2mm long) | % | Molded product: JIS No.2 | ||
ＭＦＲ ＭＦＲ/ASTM D1238 | MFR(2.16kg,200℃) | ASTM D1238 | g/10min | 13 | - |
| Key Features |
|---|
Functional grade, good adhesion, low warping |