| Manufacturer | LANXESS K.K. |
| Resin Name | PBT |
| Product Name | Pocan |
| ISO Material Code | ISO 20028-PBT,GHMRW,09-030 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (23℃) | ISO 1183 | g/cm^3 | 1.29 | - |
Bulk density (23℃) | ISO 60 | g/cm^3 | 0.8 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1,-2 | Deflection temperature under load (1.80MPa) | ISO 75-1,-2 | ℃ | 75 | - |
Deflection temperature under load (0.45MPa) | ISO 75-1,-2 | ℃ | 140 | - | |
Melting point Melting point/ISO 11357-1,-3 | Melting point (10℃/min) | ISO 11357-1,-3 | ℃ | 225 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527-1,-2 | Tensile yield stress (50mm/min) | ISO 527-1,-2 | MPa | 55 | - |
Tensile Modulus Tensile Modulus/ISO 527-1,-2 | Tensile modulus (1mm/min) | ISO 527-1,-2 | MPa | 2600 | - |
Bending strength Bending strength/ISO 178-A | Bending strength (2mm/min) | ISO 178-A | MPa | 85 | - |
Bending stress at 3.5% displacement (2mm/min) | ISO 178-A | MPa | 75 | - | |
Flexural modulus Flexural modulus/ISO 178-A | Flexural modulus (2mm/min) | ISO 178-A | MPa | 2600 | - |
Charpy impact strength Charpy impact strength/ISO 179-1eU | Charpy impact strength (23℃) | ISO 179-1eU | kJ/m^2 | 150 | - |
Charpy impact strength (-30℃) | ISO 179-1eU | kJ/m^2 | 100 | - | |
Charpy impact strength (notched, 23℃) | ISO 179-1eA | kJ/m^2 | 10 | - | |
Izod impact strength Izod impact strength/ISO 180-1U | Izod impact strength (23℃) | ISO 180-1U | kJ/m^2 | 120 | - |
Izod impact strength (-30℃) | ISO 180-1U | KJ/m^2 | 65 | - | |
Izod impact strength (notched, 23℃) | ISO 180-1A | KJ/m^2 | 10 | < Less than | |
Tensile elongation Tensile elongation/ISO 527-1,-2 | Tensile yield elongation (50mm/min) | ISO 527-1,-2 | % | 3.5 | - |
Yield Strain Yield Strain/ISO 178-A | Bending strain at bending strength (2mm/min) | ISO 178-A | % | 5.6 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294-4 | Mold shrinkage (parallel direction, 60x60x2, 250℃/WZ80℃, 600bar) | ISO 294-4 | % | 2.1 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 294-4 | Mold shrinkage (vertical direction, 60x60x2, 250℃/WZ80℃, 600bar) | ISO 294-4 | % | 2.1 | - |
MVR MVR/ISO 1133-1 | MVR(260℃,2.16kg) | ISO 1133-1 | cm^3/10min | 50 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 120 | 4-8hr |
| Key Features |
|---|
Unreinforced, injection molding grade, hydrolysis resistant |