| Manufacturer | LANXESS K.K. |
| Resin Name | PBT |
| Product Name | Pocan |
| ISO Material Code | ISO 20028-PBT,GF20,GHMR,09-070 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (23℃) | ISO 1183 | g/cm^3 | 1.44 | - |
Bulk density (23℃) | ISO 60 | g/cm^3 | 0.7 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening temperature (50N, 120℃/h) | ISO 306 | ℃ | 210 | - |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1,-2 | Deflection temperature under load (1.80MPa) | ISO 75-1,-2 | ℃ | 205 | - |
Deflection temperature under load (0.45MPa) | ISO 75-1,-2 | ℃ | 220 | - | |
Melting point Melting point/ISO 11357-1,-3 | Melting point (10℃/min) | ISO 11357-1,-3 | ℃ | 225 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO 527-1,-2 | Tensile breaking strength (5mm/min) | ISO 527-1,-2 | MPa | 120 | - |
Tensile strain at break Tensile strain at break/ISO 527-1,-2 | Tensile elongation at break (5mm/min) | ISO 527-1,-2 | % | 3.2 | - |
Tensile Modulus Tensile Modulus/ISO 527-1,-2 | Tensile modulus (1mm/min) | ISO 527-1,-2 | MPa | 7100 | - |
Bending strength Bending strength/ISO 178-A | Bending strength (2mm/min) | ISO 178-A | MPa | 195 | - |
Bending stress at 3.5% displacement (2mm/min) | ISO 178-A | MPa | 195 | - | |
Flexural modulus Flexural modulus/ISO 178-A | Flexural modulus (2mm/min) | ISO 178-A | MPa | 7000 | - |
Izod impact strength Izod impact strength/ISO 180-1U | Izod impact strength (23℃) | ISO 180-1U | kJ/m^2 | 35 | - |
Yield Strain Yield Strain/ISO 178-A | Bending strain at bending strength (2mm/min) | ISO 178-A | % | 3.6 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294-4 | Mold shrinkage (parallel direction, 60x60x2, 260℃/MT80℃, 600bar) | ISO 294-4 | % | 0.5 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 294-4 | Mold shrinkage (vertical direction, 60x60x2, 260℃/MT80℃, 600bar) | ISO 294-4 | % | 1 | - |
MVR MVR/ISO 1133-1 | MVR(260℃,2.16kg) | ISO 1133-1 | cm^3/10min | 20 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 120 | 4-8hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 20 | GF |
| Key Features |
|---|
Injection molding grade, laser transmittance, near infrared laser transmittance (black) |