| Manufacturer | LANXESS K.K. |
| Resin Name | PBT |
| Product Name | Pocan |
| ISO Material Code | ISO 20028-PBT+PC,GHPR,11-020 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (23℃) | ISO 1183 | g/cm^3 | 1.2 | - |
Bulk density (23℃) | ISO 60 | g/cm^3 | 0.75 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening temperature (50N, 50℃/h) | ISO 306 | ℃ | 121 | - |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1,-2 | Deflection temperature under load (1.80MPa) | ISO 75-1,-2 | ℃ | 89 | - |
Deflection temperature under load (0.45MPa) | ISO 75-1,-2 | ℃ | 108 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-1,-2 | Linear expansion coefficient (parallel direction) (23℃-55℃) | ISO 11359-1,-2 | x10^-5/℃ | 8.9 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ISO 11359-1,-2 | Linear expansion coefficient (vertical direction) (23℃-55℃) | ISO 11359-1,-2 | x10^-5/℃ | 9.3 | - |
Melting point Melting point/ISO 11357-1,-3 | Melting point (10℃/min) | ISO 11357-1,-3 | ℃ | 225 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527-1,-2 | Tensile yield stress (50mm/min) | ISO 527-1,-2 | MPa | 55 | - |
Tensile Modulus Tensile Modulus/ISO 527-1,-2 | Tensile modulus (1mm/min) | ISO 527-1,-2 | MPa | 2500 | - |
Bending strength Bending strength/ISO 178-A | Bending strength (2mm/min) | ISO 178-A | MPa | 80 | - |
Bending stress at 3.5% displacement (2mm/min) | ISO 178-A | MPa | 75 | - | |
Flexural modulus Flexural modulus/ISO 178-A | Flexural modulus (2mm/min) | ISO 178-A | MPa | 2200 | - |
Charpy impact strength Charpy impact strength/ISO 179-1eU | Charpy impact strength (23℃) | ISO 179-1eU | kJ/m^2 | NB | |
Charpy impact strength (notched, 23℃) | ISO 179-1eA | kJ/m^2 | 60 | - | |
Charpy impact strength (notched, -30℃) | ISO 179-1eA | kJ/m^2 | 23 | - | |
Izod impact strength Izod impact strength/ISO 180-1U | Izod impact strength (23℃) | ISO 180-1U | kJ/m^2 | NB | |
Izod impact strength (notched, 23℃) | ISO 180-1A | KJ/m^2 | 55 | - | |
Izod impact strength (notched, -30℃) | ISO 180-1A | KJ/m^2 | 20 | - | |
Tensile elongation Tensile elongation/ISO 527-1,-2 | Tensile yield elongation (50mm/min) | ISO 527-1,-2 | % | 4.2 | - |
Yield Strain Yield Strain/ISO 178-A | Bending strain at bending strength (2mm/min) | ISO 178-A | % | 5.5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294-4 | Mold shrinkage (parallel direction, 60x60x2, 250℃/WZ70℃, 600bar) | ISO 294-4 | % | 0.8 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 294-4 | Mold shrinkage (vertical direction, 60x60x2, 250℃/WZ70℃, 600bar) | ISO 294-4 | % | 0.8 | - |
MVR MVR/ISO 1133-1 | MVR(260℃,5kg) | ISO 1133-1 | cm^3/10min | 25 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 120 | 4-8hr |
| Key Features |
|---|
PBT+PC, unreinforced, injection molding grade, low warpage, excellent appearance, impact resistance |