| Manufacturer | LANXESS K.K. |
| Resin Name | PBT |
| Product Name | Pocan |
| ISO Material Code | ISO 20028-PBT+PC,GF20,GHMR,09-050 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (23℃) | ISO 1183 | g/cm^3 | 1.4 | - |
Bulk density (23℃) | ISO 60 | g/cm^3 | 0.7 | - | |
Water absorption Water absorption/ISO 62 | Water absorption (at equilibrium) (23℃, 50%RH) | ISO 62 | % | 0.1 | - |
Water absorption (when saturated) (23℃ water) | ISO 62 | % | 0.3 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening temperature (50N, 120℃/h) | ISO 306 | ℃ | 145 | - |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1,-2 | Deflection temperature under load (1.80MPa) | ISO 75-1,-2 | ℃ | 110 | - |
Melting point Melting point/ISO 11357-1,-3 | Melting point (10℃/min) | ISO 11357-1,-3 | ℃ | 225 | - |
Flammability Flammability/UL 94 | Combustion Test | UL 94 | NaN | 0.75mm | |
Combustion Test | UL 94 | NaN | 1.5mm |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO 527-1,-2 | Tensile breaking strength (5mm/min) | ISO 527-1,-2 | MPa | 75 | - |
Tensile strain at break Tensile strain at break/ISO 527-1,-2 | Tensile elongation at break (5mm/min) | ISO 527-1,-2 | % | 4 | - |
Tensile Modulus Tensile Modulus/ISO 527-1,-2 | Tensile modulus (1mm/min) | ISO 527-1,-2 | MPa | 5100 | - |
Bending strength Bending strength/ISO 178-A | Bending strength (2mm/min) | ISO 178-A | MPa | 130 | - |
Flexural modulus Flexural modulus/ISO 178-A | Flexural modulus (2mm/min) | ISO 178-A | MPa | 4700 | - |
Charpy impact strength Charpy impact strength/ISO 179-1eU | Charpy impact strength (23℃) | ISO 179-1eU | kJ/m^2 | 35 | - |
Izod impact strength Izod impact strength/ISO 180-1U | Izod impact strength (23℃) | ISO 180-1U | kJ/m^2 | 30 | - |
Izod impact strength (notched, 23℃) | ISO 180-1A | KJ/m^2 | 10 | < Less than | |
Izod impact strength (notched, -30℃) | ISO 180-1A | KJ/m^2 | 10 | < Less than | |
Izod impact strength (notched, -40℃) | ISO 180-1A | KJ/m^2 | 10 | < Less than | |
Yield Strain Yield Strain/ISO 178-A | Bending strain at bending strength (2mm/min) | ISO 178-A | % | 4.5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 2577 | Mold shrinkage (parallel direction, 150×105×3, 260℃/MT80℃, 600bar) | ISO 2577 | % | 0.45 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 2577 | Mold shrinkage (vertical direction, 150×105×3, 260℃/MT80℃, 600bar) | ISO 2577 | % | 0.5 | - |
MVR MVR/ISO 1133-1 | MVR(260℃,5kg) | ISO 1133-1 | cm^3/10min | 40 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 20 | GF |
| Main Applications |
|---|
Automotive and Electrical Applications |
| Key Features |
|---|
PBT+PC, injection molding grade, low warpage, excellent appearance, laser transparency, near infrared laser transparency (black) |