| Manufacturer | LANXESS K.K. |
| Resin Name | PET |
| Product Name | Pocan |
| ISO Material Code | ISO 20028-PET+PBT,(GF+MD)40,GHMR,07-120 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (23℃) | ISO 1183 | g/cm^3 | 1.7 | - |
Bulk density (23℃) | ISO 60 | g/cm^3 | 0.9 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening temperature (50N, 120℃/h) | ISO 306 | ℃ | 220 | - |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1,-2 | Deflection temperature under load (1.80MPa) | ISO 75-1,-2 | ℃ | 205 | - |
Deflection temperature under load (0.45MPa) | ISO 75-1,-2 | ℃ | 250 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-1,-2 | Linear expansion coefficient (parallel direction) (23℃-55℃) | ISO 11359-1,-2 | x10^-5/℃ | 2 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ISO 11359-1,-2 | Linear expansion coefficient (vertical direction) (23℃-55℃) | ISO 11359-1,-2 | x10^-5/℃ | 5 | - |
Melting point Melting point/ISO 11357-1,-3 | Melting point (10℃/min) | ISO 11357-1,-3 | ℃ | 260 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO 527-1,-2 | Tensile breaking strength (5mm/min) | ISO 527-1,-2 | MPa | 125 | - |
Tensile strain at break Tensile strain at break/ISO 527-1,-2 | Tensile elongation at break (5mm/min) | ISO 527-1,-2 | % | 1.6 | - |
Tensile Modulus Tensile Modulus/ISO 527-1,-2 | Tensile modulus (1mm/min) | ISO 527-1,-2 | MPa | 12000 | - |
Bending strength Bending strength/ISO 178-A | Bending strength (2mm/min) | ISO 178-A | MPa | 175 | - |
Flexural modulus Flexural modulus/ISO 178-A | Flexural modulus (2mm/min) | ISO 178-A | MPa | 11000 | - |
Charpy impact strength Charpy impact strength/ISO 179-1eA | Charpy impact strength (notched, 23℃) | ISO 179-1eA | kJ/m^2 | 10 | - |
Charpy impact strength (notched, -30℃) | ISO 179-1eA | kJ/m^2 | 10 | - | |
Izod impact strength Izod impact strength/ISO 180-1U | Izod impact strength (23℃) | ISO 180-1U | kJ/m^2 | 35 | - |
Izod impact strength (notched, 23℃) | ISO 180-1A | KJ/m^2 | 10 | < Less than | |
Izod impact strength (notched, -30℃) | ISO 180-1A | KJ/m^2 | 10 | < Less than | |
Yield Strain Yield Strain/ISO 178-A | Bending strain at bending strength (2mm/min) | ISO 178-A | % | 2 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294-4 | Mold shrinkage (parallel direction, 60x60x2, 280℃/WZ110℃, 600bar) | ISO 294-4 | % | 0.2 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 294-4 | Mold shrinkage (vertical direction, 60x60x2, 280℃/WZ110℃, 600bar) | ISO 294-4 | % | 0.7 | - |
MVR MVR/ISO 1133-1 | MVR(280℃,2.16kg) | ISO 1133-1 | cm^3/10min | 25 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 120 | 4-8hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 40 | GF+MD |
| Main Applications |
|---|
For electronic components and lead-free reflow soldering |
| Key Features |
|---|
PET+PBT, injection molding grade, high flow, high temperature dimensional stability |