| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Density | ASTM D792 | g/cm^3 | 1.35 | - |
Water absorption Water absorption/ISO 62 | Water absorption (23℃/sat) | ISO 62 | % | 0.07 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening point (Rate A/50) | ISO 306 | ℃ | 131 | - |
Vicat softening point (Rate B/50) | ISO 306 | ℃ | 123 | - | |
Vicat softening point (Rate B/120) | ISO 306 | ℃ | 125 | - | |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Af | HDT/Af(1.8 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Af | ℃ | 117 | - |
HDT/Bf(0.45 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Bf | ℃ | 121 | - | |
HDT (0.45 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 121 | - | |
HDT (1.82 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 116 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-2 | CTE(23℃～80℃)(flow direction) | ISO 11359-2 | x10^-5/℃ | 2.6 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ISO 11359-2 | CTE (23℃～80℃) (vertical direction) | ISO 11359-2 | x10^-5/℃ | 7.3 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) (5mm/min) | ISO 527 | MPa | 112 | - |
Tensile strength (break point) (Type I, 5mm/min) | ASTEM D638 | MPa | 110 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (break point) (5mm/min) | ISO 527 | % | 2.6 | - |
Tensile elongation (break point) (Type I, 5 mm/min) | ASTM D638 | % | 2.7 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 6800 | - |
Tensile elasticity (5mm/min) | ASTM D638 | MPa | 6680 | - | |
Bending strength Bending strength/ISO 178 | Bending strength (break point) (2mm/min) | ISO 178 | MPa | 165 | - |
Flexural strength (break point) (1.3mm/min, 50mm span) | ASTM D790 | MPa | 167 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending elasticity (2mm/min) | ISO 178 | MPa | 6240 | - |
Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 6150 | - | |
Charpy impact strength Charpy impact strength/ISO 179-1eU | Sharopy strength 23℃ (Unnotch Edgew 80*10*3 sp=62mm) | ISO 179-1eU | kJ/m^2 | 55 | - |
Sharopy strength -30℃(Unnotch Edgew 80*10*3 sp=62mm) | ISO 179-1eU | kJ/m^2 | 67 | - | |
Sharopy strength 23℃ (Unnotch Edgew 80*10*4 sp=62mm) | ISO 179-1eU | kJ/m^2 | 59 | - | |
Sharoppy strength 23℃(V-notch Edgew 80*10*3 sp=62mm) | ISO 179-1eA | kJ/m^2 | 15 | - | |
Sharopy strength -30℃(V-notch Edgew 80*10*3 sp=62mm) | ISO 179-1eA | kJ/m^2 | 10 | - | |
Sharoppy strength 23℃ (V-notch Edgew 80*10*4 sp=62mm) | ISO 179-1eA | kJ/m^2 | 14 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 13 | - |
Izod impact strength (notched, 80*10*4 -30℃) | ISO 180/1A | kJ/m^2 | 9 | - | |
Izod impact strength (notched, 80*10*3 +23℃) | ISO 180/1A | kJ/m^2 | 13 | - | |
Izod impact strength (notched, 80*10*3 -30℃) | ISO 180/1A | kJ/m^2 | 9 | - | |
Izod impact strength (unnotched, 80*10*4 +23℃) | ISO 180/1U | kJ/m^2 | 48 | - | |
Izod impact strength (unnotched, 80*10*3 +23℃) | ISO 180/1U | kJ/m^2 | 48 | - | |
Izod impact strength (unnotched, 80*10*3 -30℃) | ISO 180/1U | kJ/m^2 | 54 | - | |
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 150 | - | |
Izod impact strength (unnotched, 23℃) | ASTM D4812 | J/m | 715 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Dielectric constant Dielectric constant/SABIC method | Dielectric constant, 1.1GHz | SABIC method | - | 3.24 | - |
Dielectric constant, 1.9GHz | SABIC method | - | 3.28 | - | |
Dielectric constant, 5GHz | SABIC method | - | 3.28 | - | |
Dielectric constant, 10GHz | SABIC method | - | 3.27 | - | |
Dielectric Strength Dielectric Strength/IEC 60243-1 | Dielectric breakdown strength (in oil) (1.0mm) | IEC 60243-1 | kV/mm | 40 | - |
Arc Resistance Arc Resistance/ASTM D495 | Arc Resistance, Tungsten (PLC) | ASTM D495 | PLC Code | 7 | D495<60 |
Tracking resistance Tracking resistance/UL 746A | CTI(Comparative Tracking Index)(UL,PLC) | UL 746A | PLC Code | 3 | 175≦CTI<250 |
CTI(Comparative Tracking Index) | IEC 60112 | V | 200 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ASTM D955 | Mold shrinkage rate (flow direction) (24 hours) | ASTM D955 | % | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/ASTM D955 | Mold shrinkage (vertical direction) (24 hours) | ASTM D955 | % | - | |
ＭＦＲ ＭＦＲ/ASTM D1238 | Melt flow rate (300℃/1.2kgf) | ASTM D1238 | g/10min | 12 | - |
Melt flow rate (300℃/2.16kgf) | ASTM D1238 | g/10min | 24 | - | |
ＭＶＲ ＭＶＲ/ISO 1133 | Melt volume rate (300℃/1.2kgf) | ISO 1133 | cm3/10min | 10 | - |
Melt volume rate (300℃/2.16kgf) | ISO 1133 | cm3/10min | 20 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 110 | 3-6hr |
| Key Features |
|---|
Flame retardant, high rigidity, high toughness, glass fiber reinforced |