| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PC resin |
| Product Name | STAT-KON COMPOUND |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Density | ASTM D792 | g/cm^3 | 1.24 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Af | HDT/Af(1.8 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Af | ℃ | 127 | - |
HDT (0.45 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 138 | - | |
HDT (1.82 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 127 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point) | ISO 527 | MPa | 60 | - |
Tensile strength (yield point) | ASTM D638 | MPa | 62 | - | |
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) | ISO 527 | MPa | 53 | - |
Tensile strength (break point) | ASTEM D638 | MPa | 56 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (at break) | ISO 527 | % | 8.8 | - |
Tensile elongation (break point) (Type I, 5 mm/min) | ASTM D638 | % | 9.5 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 2900 | - |
Tensile elasticity (50mm/min) | ASTM D638 | MPa | 2680 | - | |
Bending strength Bending strength/ISO 178 | Bending strength | ISO 178 | MPa | 102 | - |
Bending strength | ASTM D790 | MPa | 102 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending Elasticity | ISO 178 | MPa | 3100 | - |
Bending Elasticity | ASTM D790 | MPa | 2890 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 6 | - |
Izod impact strength (unnotched, 80*10*4 +23℃) | ISO 180/1U | kJ/m^2 | 98 | - | |
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 64 | - | |
Izod impact strength (unnotched, 23℃) | ASTM D4812 | J/m | 1217 | - | |
Tensile elongation Tensile elongation/ISO 527 | Tensile elongation (yield point) | ISO 527 | % | 4.4 | - |
Tensile elongation (yield point) | ASTM D638 | % | 4.9 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Surface resistance Surface resistance/ASTM D257 | Surface resistance | ASTM D257 | Ω | 1×10^2 ~ 1×10^6 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294 | Mold shrinkage rate (flow direction) (24 hours) | ISO 294 | % | 0.84 | - |
Mold shrinkage rate (flow direction) (24 hours) | ASTM D955 | % | 0.8 | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 294 | Mold shrinkage (vertical direction) (24 hours) | ISO 294 | % | 0.82 | - |
Mold shrinkage (vertical direction) (24 hours) | ASTM D955 | % | 0.8 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 120 | 4hr |
| Key Features |
|---|
Conductive, carbon powder |