| Manufacturer | SABIC - SHPP Japan |
| Resin Name | POM resin |
| Product Name | STAT-KON COMPOUND |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density | ISO 1183 | g/cm^3 | 1.45 | - |
Density | ASTM D792 | g/cm^3 | 1.45 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Af | HDT/Af(1.8 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Af | ℃ | 105 | - |
HDT (1.82 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 108 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-2 | CTE(-40℃～+40℃)(flow direction) | ISO 11359-2 | x10^-5/℃ | 10.2 | - |
CTE(-40℃～+40℃)(flow direction) | ASTM E831 | x10^-5/℃ | 10.1 | - | |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ISO 11359-2 | CTE (-40℃～+40℃)(vertical direction) | ISO 11359-2 | x10^-5/℃ | 10.1 | - |
CTE (-40℃～+40℃)(vertical direction) | ASTM E831 | x10^-5/℃ | 10.1 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point) | ISO 527 | MPa | 53 | - |
Tensile strength (yield point) | ASTM D638 | MPa | 58 | - | |
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) | ISO 527 | MPa | 47 | - |
Tensile strength (break point) | ASTEM D638 | MPa | 54 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (at break) | ISO 527 | % | 20 | - |
Tensile elongation (at break) | ASTM D638 | % | 7.2 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 3000 | - |
Tensile elasticity (50mm/min) | ASTM D638 | MPa | 3500 | - | |
Bending strength Bending strength/ISO 178 | Bending strength | ISO 178 | MPa | 82 | - |
Bending strength | ASTM D790 | MPa | 95 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending Elasticity | ISO 178 | MPa | 3200 | - |
Bending Elasticity | ASTM D790 | MPa | 3250 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 5 | - |
Izod impact strength (unnotched, 80*10*4 +23℃) | ISO 180/1U | kJ/m^2 | 37 | - | |
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 35 | - | |
Izod impact strength (unnotched, 23℃) | ASTM D4812 | J/m | 800 | - | |
Tensile elongation Tensile elongation/ISO 527 | Tensile elongation (yield point) | ISO 527 | % | 5 | - |
Tensile elongation (yield point) | ASTM D638 | % | 3.6 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Surface resistance Surface resistance/ASTM D257 | Surface resistance | ASTM D257 | Ω | 1×10^2 ~ 1×10^4 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294 | Mold shrinkage rate (flow direction) (24 hours) | ISO 294 | % | - | |
Mold shrinkage rate (flow direction) (24 hours) | ASTM D955 | % | - | ||
Mold shrinkage rate (flow direction) (mold temp=60℃) | SABIC method | % | - | ||
Mold shrinkage rate (flow direction) (mold temp=100℃) | SABIC method | % | - | ||
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 294 | Mold shrinkage (vertical direction) (24 hours) | ISO 294 | % | - | |
Mold shrinkage (vertical direction) (24 hours) | ASTM D955 | % | - | ||
Mold shrinkage (vertical direction) (mold temp=60℃) | SABIC method | % | - | ||
Mold shrinkage (vertical direction) (mold temp=100℃) | SABIC method | % | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 80 | 4hr |
| Key Features |
|---|
Conductivity |