| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PC resin |
| Product Name | KONDUIT COMPOUND |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Density | ASTM D792 | g/cm^3 | 1.46 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Af | HDT/Af(1.8 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Af | ℃ | 119 | - |
HDT/Bf(0.45 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Bf | ℃ | 128 | - | |
HDT(0.45 MPa,3.2mm) | ASTM D648 | ℃ | 127 | - | |
HDT (1.82 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 121 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTM E831 | CTE(40℃～+120℃)(flow direction) | ASTM E831 | x10^-5/℃ | 5.3 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ASTM E831 | CTE (40℃～120℃) (vertical direction) | ASTM E831 | x10^-5/℃ | 8.5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) (5mm/min) | ISO 527 | MPa | 42 | - |
Tensile strength (break point) (Type I, 5mm/min) | ASTEM D638 | MPa | 41 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (break point) (5mm/min) | ISO 527 | % | 4.1 | - |
Tensile elongation (break point) (Type I, 5 mm/min) | ASTM D638 | % | 5 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 3880 | - |
Tensile elasticity (5mm/min) | ASTM D638 | MPa | 3830 | - | |
Bending strength Bending strength/ISO 178 | Bending strength (break point) (2mm/min) | ISO 178 | MPa | 81 | - |
Flexural strength (break point) (1.3mm/min, 50mm span) | ASTM D790 | MPa | 77 | - | |
Bending strength (yield point) (1.3mm/min, 50mm span) | ASTM D790 | MPa | 79 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending elasticity (2mm/min) | ISO 178 | MPa | 4180 | - |
Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 3160 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 13 | - |
Izod impact strength (unnotched, 80*10*4 +23℃) | ISO 180/1U | kJ/m^2 | 41 | - | |
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 150 | - | |
Izod impact strength (unnotched, 23℃) | ASTM D4812 | J/m | 700 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Dielectric constant Dielectric constant/ASTM ES7-83 | Dielectric constant (DK), 1.1GHz | ASTM ES7-83 | - | 3.66 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ASTM D955 | Mold shrinkage rate (flow direction) (24 hours) | ASTM D955 | % | 0.41 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ASTM D955 | Mold shrinkage (vertical direction) (24 hours) | ASTM D955 | % | 0.39 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 120 | 2-4hr |
| Key Features |
|---|
Thermally conductive, shock resistant, mineral reinforced |