| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPE resin |
| Product Name | LUBRILOY COMPOUND |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Density | ASTM D792 | g/cm^3 | 1.1 | - |
Proportion | ASTM D792 | 1.1 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Af | HDT/Af(1.8 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Af | ℃ | 99 | - |
HDT/Bf(0.45 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Bf | ℃ | 116 | - | |
HDT (0.45 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 120 | - | |
HDT (1.82 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 105 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTM D696 | CTE(-30℃～+30℃)(flow direction) | ASTM D696 | x10^-5/℃ | 8.7 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ASTM D696 | CTE(-30℃～+30℃)(vertical direction) | ASTM D696 | x10^-5/℃ | 9.8 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point) (5mm/min) | ISO 527 | MPa | 58 | - |
Tensile strength (yield point) (Type I, 5 mm/min) | ASTM D638 | MPa | 57 | - | |
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) (5mm/min) | ISO 527 | MPa | 49 | - |
Tensile strength (break point) (Type I, 5mm/min) | ASTEM D638 | MPa | 48 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (break point) (5mm/min) | ISO 527 | % | 24 | - |
Tensile elongation (break point) (Type I, 5 mm/min) | ASTM D638 | % | 40 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 2000 | - |
Tensile elasticity (5mm/min) | ASTM D638 | MPa | 2120 | - | |
Bending strength Bending strength/ISO 178 | Bending strength | ISO 178 | MPa | 74 | - |
Flexural modulus Flexural modulus/ISO 178 | Bending elasticity (2mm/min) | ISO 178 | MPa | 1920 | - |
Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 2130 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 31 | - |
Izod impact strength (unnotched, 80*10*4 +23℃) | ISO 180/1U | kJ/m^2 | 210 | - | |
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 419 | - | |
Izod impact strength (unnotched, 23℃) | ASTM D4812 | J/m | 2110 | - | |
Tensile elongation Tensile elongation/ISO 527 | Tensile elongation (yield point) (5mm/min) | ISO 527 | % | 5 | - |
Tensile elongation (yield point) (Type I, 5mm/min) | ASTM D638 | % | 5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ASTM D955 | Mold shrinkage rate (flow direction) (24 hours) | ASTM D955 | % | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/ASTM D955 | Mold shrinkage (vertical direction) (24 hours) | ASTM D955 | % | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 80 | 4hr |
| Key Features |
|---|
Sliding wear resistance |