| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPS resin |
| Product Name | LUBRICOMP COMPOUND |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Density | ASTM D792 | g/cm^3 | 1.51 | - |
Water absorption Water absorption/ISO 62-1 | Water absorption (23℃/24h) | ISO 62-1 | % | 0.4 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ASTM D648 | HDT (1.82 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 260 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point) (5mm/min) | ISO 527 | MPa | 166 | - |
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) (5mm/min) | ISO 527 | MPa | 166 | - |
Tensile strength (break point) | ASTEM D638 | 253 | - | ||
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (break point) (5mm/min) | ISO 527 | % | 0.9 | - |
Tensile elongation (at break) | ASTM D638 | % | 1.6 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 24890 | - |
Tensile elasticity (5mm/min) | ASTM D638 | MPa | 26120 | - | |
Bending strength Bending strength/ISO 178 | Bending strength (break point) (2mm/min) | ISO 178 | MPa | 254 | - |
Bending strength (yield point) (2mm/min) | ISO 178 | MPa | 254 | - | |
Bending strength | ASTM D790 | MPa | 253 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending elasticity (2mm/min) | ISO 178 | MPa | 22240 | - |
Bending Elasticity | ASTM D790 | MPa | 21400 | - | |
Izod impact strength Izod impact strength/ASTM D256 | Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 53 | - |
Izod impact strength (unnotched, 23℃) | ASTM D4812 | J/m | 485 | - | |
Yield Strain Yield Strain/ISO 178 | Bending strain (2mm/min) | ISO 178 | % | 1.4 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Surface resistance Surface resistance/ASTM D257 | Surface resistance | ASTM D257 | Ω | NaN | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ASTM D955 | Mold shrinkage rate (flow direction) (24 hours) | ASTM D955 | % | 0.2 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ASTM D955 | Mold shrinkage (vertical direction) (24 hours) | ASTM D955 | % | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 4hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 45 | CF+PTFE |
| Key Features |
|---|
Sliding wear resistance |