| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPA Resin |
| Product Name | LUBRICOMP COMPOUND |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density | ISO 1183 | g/cm^3 | 1.42 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Af | HDT/Af(1.8 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Af | ℃ | 270 | - |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-2 | CTE(23℃～60℃)(flow direction) | ISO 11359-2 | x10^-5/℃ | 0.8 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ISO 11359-2 | CTE (23℃～60℃) (vertical direction) | ISO 11359-2 | x10^-5/℃ | 5.1 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) (5mm/min) | ISO 527 | MPa | 256 | - |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (break point) (5mm/min) | ISO 527 | % | 1.3 | - |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 25100 | - |
Bending strength Bending strength/ISO 178 | Bending strength (yield point) (2mm/min) | ISO 178 | MPa | 340 | - |
Flexural modulus Flexural modulus/ISO 178 | Bending elasticity (2mm/min) | ISO 178 | MPa | 19900 | - |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 7 | - |
Izod impact strength (unnotched, 80*10*4 +23℃) | ISO 180/1U | kJ/m^2 | 40 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Surface resistance Surface resistance/ASTM D257 | Surface resistance | ASTM D257 | Ω | 1×10^1 ~ 1×10^3 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) | SABIC method | % | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 4hr |
| Key Features |
|---|
Sliding wear resistance |