| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPE/PS |
| Product Name | NORYL |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Proportion | ASTM D792 | 1.08 | - | |
Water absorption Water absorption/ASTM D570 | Water absorption rate (24 hours) | ASTM D570 | % | 0.07 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ASTM D648 | HDT (1.82 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 147 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/SABIC Method | Tensile strength (yield point) | SABIC Method | MPa | 81 | - |
Tensile strain at break Tensile strain at break/SABIC Method | Tensile elongation (at break) | SABIC Method | % | 80 | - |
Bending strength Bending strength/ASTM D790 | Bending strength | ASTM D790 | MPa | 119 | - |
Flexural modulus Flexural modulus/ASTM D790 | Bending Elasticity | ASTM D790 | MPa | 2800 | - |
Izod impact strength Izod impact strength/ASTM D256 | Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 31 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) (3.2mm) | SABIC method | % | - | |
ＭＦＲ ＭＦＲ/ASTM D1238 | Melt flow rate (300℃/5.0kgf) | ASTM D1238 | g/10min | 14.2 | - |