| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPE/PS |
| Product Name | NORYL |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Proportion | ASTM D792 | 1.13 | - | |
Water absorption Water absorption/ASTM D570 | Water absorption rate (24 hours) | ASTM D570 | % | 0.06 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening point (Rate B/50) | ISO 306 | ℃ | 131 | - |
Vicat softening point (Rate B/120) | ISO 306 | ℃ | 134 | - | |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Ae | HDT/Ae(1.8 MPa Edgew 120*10*4 sp=100mm) | ISO 75/Ae | ℃ | 124 | - |
HDT/Be(0.45 MPa Edgew 120*10*4 sp=100mm) | ISO 75/Be | ℃ | 132 | - | |
HDT (0.45 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 131 | - | |
HDT (1.82 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 122 | - | |
HDT (1.82 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 125 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTM E831 | CTE(-40℃～+40℃)(flow direction) | ASTM E831 | x10^-5/℃ | 5.12 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ASTM E831 | CTE (-40℃～+40℃)(vertical direction) | ASTM E831 | x10^-5/℃ | 7.14 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) | ISO 527 | MPa | 64 | - |
Tensile strength (break point) (Type I, 5mm/min) | ASTEM D638 | MPa | 63 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (at break) | ISO 527 | % | 3 | - |
Tensile elongation (at break) | ASTM D638 | % | 3 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 4400 | - |
Tensile elasticity (5mm/min) | ASTM D638 | MPa | 4350 | - | |
Bending strength Bending strength/ISO 178 | Bending strength | ISO 178 | MPa | 122 | - |
Bending strength (yield point) (1.3mm/min, 50mm span) | ASTM D790 | MPa | 116 | - | |
Bending strength (yield point) (2.6mm/min, 100mm span) | ASTM D790 | MPa | 107 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending Elasticity | ISO 178 | MPa | 4160 | - |
Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 3840 | - | |
Bending elasticity (2.6mm/min, 100mm span) | ASTM D790 | MPa | 3580 | - | |
Charpy impact strength Charpy impact strength/ISO 179-1eU | Sharopy strength 23℃ (Unnotch Edgew 80*10*4 sp=62mm) | ISO 179-1eU | kJ/m^2 | 34 | - |
Shalopy strength (notched, 23℃) | ISO 179/2C | kJ/m^2 | 11 | - | |
Shalopy strength (unnotched, -30℃) | ISO 179/2C | kJ/m^2 | 9 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 10 | - |
Izod impact strength (notched, 80*10*4 -30℃) | ISO 180/1A | kJ/m^2 | 9 | - | |
Izod impact strength (unnotched, 80*10*4 +23℃) | ISO 180/1U | kJ/m^2 | 27 | - | |
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 118 | - | |
Izod impact strength (notched, -30℃) | ASTM D256 | J/m | 103 | - | |
Izod impact strength (unnotched, 23℃) | ASTM D4812 | J/m | 449 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Dielectric constant Dielectric constant/ASTM D150 | Dielectric constant, 1MHz | ASTM D150 | - | 2.9 | - |
Arc Resistance Arc Resistance/ASTM D495 | Arc Resistance, Tungsten (PLC) | ASTM D495 | PLC Code | 7 | D495<60 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) (3.2mm) | SABIC method | % | - | |
ＭＦＲ ＭＦＲ/ASTM D1238 | Melt flow rate (300℃/5.0kgf) | ASTM D1238 | g/10min | 16.6 | - |
ＭＶＲ ＭＶＲ/ISO 1133 | Melt volume rate (300℃/5.0kgf) | ISO 1133 | cm3/10min | 16 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 3-4hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 10 | GF |
| Main Applications |
|---|
Construction field, indoor and outdoor use, display, lawn and garden equipment |
| Key Features |
|---|
Glass fiber reinforced, high strength, dimensionally stable |