| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPE/PS |
| Product Name | NORYL |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Proportion | ASTM D792 | 1.13 | - | |
Water absorption Water absorption/ASTM D570 | Water absorption rate (24 hours) | ASTM D570 | % | 0.01 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ASTM D1525 | Vicat softening point (Rate B/50) | ASTM D1525 | ℃ | 136 | - |
Deflection Temperature under Load Deflection Temperature under Load/ASTM D648 | HDT(1.82 MPa,3.2mm) | ASTM D648 | ℃ | 124 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ASTEM D638 | Tensile strength (break point) (Type I, 5mm/min) | ASTEM D638 | MPa | 68 | - |
Tensile strain at break Tensile strain at break/ASTM D638 | Tensile elongation (break point) (Type I, 5 mm/min) | ASTM D638 | % | 5 | - |
Flexural modulus Flexural modulus/ASTM D790 | Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 3500 | - |
Izod impact strength Izod impact strength/ASTM D256 | Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 93 | - |
Izod impact strength (notched, -30℃) | ASTM D256 | J/m | 77 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Volume resistivity Volume resistivity/ASTM D257 | Volume Resistivity | ASTM D257 | Ω・cm | NaN | - |
Dielectric constant Dielectric constant/ASTM D150 | Specific dielectric rate, 1GHz | ASTM D150 | - | 2.7 | - |
Dielectric constant, 100MHz | IEC 60250 | - | 2.7 | - | |
Tracking resistance Tracking resistance/UL 746A | CTI(Comparative Tracking Index)(UL,PLC) | UL 746A | PLC Code | 2 | 250≦CTI<400 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) (3.2mm) | SABIC method | % | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 3-4hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 7 | GF |
| Key Features |
|---|
Glass Fiber Reinforced Blend |