| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPE/PS |
| Product Name | NORYL |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Proportion | ASTM D792 | 1.25 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening point (Rate B/50) | ISO 306 | ℃ | 132 | - |
Vicat softening point (Rate B/120) | ISO 306 | ℃ | 136 | - | |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Ae | HDT/Ae(1.8 MPa Edgew 120*10*4 sp=100mm) | ISO 75/Ae | ℃ | 111 | - |
HDT/Be(0.45 MPa Edgew 120*10*4 sp=100mm) | ISO 75/Be | ℃ | 126 | - | |
HDT (0.45 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 117 | - | |
HDT (0.45 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 128 | - | |
HDT (1.82 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 108 | - | |
HDT (1.82 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 116 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTM E831 | CTE(-40℃～+40℃)(flow direction) | ASTM E831 | x10^-5/℃ | 7.06 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ASTM E831 | CTE (-40℃～+40℃)(vertical direction) | ASTM E831 | x10^-5/℃ | 7.76 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point) | ISO 527 | MPa | 71 | - |
Tensile strength (yield point) (Type I, 5 mm/min) | ASTM D638 | MPa | 74 | - | |
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) | ISO 527 | MPa | 57 | - |
Tensile strength (break point) (Type I, 5mm/min) | ASTEM D638 | MPa | 60 | - | |
Tensile strain at break Tensile strain at break/ASTM D638 | Tensile elongation (break point) (Type I, 5 mm/min) | ASTM D638 | % | 8.4 | - |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 4000 | - |
Tensile elasticity (5mm/min) | ASTM D638 | MPa | 3650 | - | |
Bending strength Bending strength/ISO 178 | Bending strength | ISO 178 | MPa | 117 | - |
Flexural strength (break point) (1.3mm/min, 50mm span) | ASTM D790 | MPa | 117 | - | |
Bending strength (yield point) (2.6mm/min, 100mm span) | ASTM D790 | MPa | 117 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending Elasticity | ISO 178 | MPa | 3800 | - |
Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 3670 | - | |
Bending elasticity (2.6mm/min, 100mm span) | ASTM D790 | MPa | 3550 | - | |
Charpy impact strength Charpy impact strength/ISO 179/2C | Shalopy strength (notched, 23℃) | ISO 179/2C | kJ/m^2 | 10 | - |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 9 | - |
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 131 | - | |
Izod impact strength (reverse notched, 3.2 mm) | ASTM D256 | J/m | 811 | - | |
Izod impact strength (unnotched, 23℃) | ASTM D4812 | J/m | 2230 | - | |
Tensile elongation Tensile elongation/ISO 527 | Tensile elongation (yield point) | ISO 527 | % | 3.7 | - |
Tensile elongation (yield point) | ASTM D638 | % | 3.8 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Volume resistivity Volume resistivity/ASTM D257 | Volume Resistivity | ASTM D257 | Ω・cm | NaN | - |
Surface resistance Surface resistance/ASTM D257 | Surface resistance | ASTM D257 | Ω | NaN | - |
Dielectric constant Dielectric constant/ASTM D150 | Dielectric constant, 1MHz | ASTM D150 | - | 2.7 | - |
Dielectric constant, 50/60Hz | ASTM D150 | - | 2.89 | - | |
Dielectric Strength Dielectric Strength/ASTM D149 | Dielectric breakdown strength (in oil) (3.2mm) | ASTM D149 | kV/mm | 17.3 | - |
Arc Resistance Arc Resistance/ASTM D495 | Arc Resistance, Tungsten (PLC) | ASTM D495 | PLC Code | 6 | 60≦D495<120 |
Tracking resistance Tracking resistance/UL 746A | CTI(Comparative Tracking Index)(UL,PLC) | UL 746A | PLC Code | 2 | 250≦CTI<400 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
ＭＦＲ ＭＦＲ/ASTM D1238 | Melt flow rate (280℃/5.0kgf) | ASTM D1238 | g/10min | 7.6 | - |
Melt flow rate (300℃/5.0kgf) | ASTM D1238 | g/10min | 7.6 | - | |
ＭＶＲ ＭＶＲ/ISO 1133 | Melt volume rate (280℃/5.0kgf) | ISO 1133 | cm3/10min | 6 | - |
Melt volume rate (300℃/5.0kgf) | ISO 1133 | cm3/10min | 6 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 3-4hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 17 | MD |
| Main Applications |
|---|
Air conditioner parts, smoke detectors, electronic/electrical indoor and outdoor applications |
| Key Features |
|---|
Flame retardant, mineral reinforced, electrical performance, dimensional stability |