| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPE/PS |
| Product Name | NORYL |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Proportion | ASTM D792 | 1.1 | - | |
Water absorption Water absorption/ASTM D570 | Water absorption rate (24 hours) | ASTM D570 | % | 0.06 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ASTM D648 | HDT (0.45 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 126 | - |
HDT (1.82 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 118 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ASTM D638 | Tensile strength (yield point) (Type I, 50 mm/min) | ASTM D638 | MPa | 65 | - |
Tensile breaking stress Tensile breaking stress/ASTEM D638 | Tensile strength (break point) (Type I, 50 mm/min) | ASTEM D638 | MPa | 53 | - |
Tensile strain at break Tensile strain at break/ASTM D638 | Tensile elongation (break point) (Type I, 50 mm/min) | ASTM D638 | % | 15 | - |
Bending strength Bending strength/ASTM D790 | Bending strength (yield point) (2.6mm/min, 100mm span) | ASTM D790 | MPa | 100 | - |
Flexural modulus Flexural modulus/ASTM D790 | Bending elasticity (2.6mm/min, 100mm span) | ASTM D790 | MPa | 2400 | - |
Izod impact strength Izod impact strength/ASTM D256 | Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 180 | - |
Izod impact strength (notched, -30℃) | ASTM D256 | J/m | 106 | - | |
Tensile elongation Tensile elongation/ASTM D638 | Tensile elongation (yield point) (Type I, 50 mm/min) | ASTM D638 | % | 4 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Volume resistivity Volume resistivity/ASTM D257 | Volume Resistivity | ASTM D257 | Ω・cm | NaN | - |
Surface resistance Surface resistance/ASTM D257 | Surface resistance | ASTM D257 | Ω | NaN | - |
Dielectric constant Dielectric constant/ASTM D150 | Dielectric constant, 1MHz | ASTM D150 | - | 2.46 | - |
Dielectric constant, 50/60Hz | ASTM D150 | - | 2.52 | - | |
Dielectric Strength Dielectric Strength/ASTM D149 | Dielectric breakdown strength (in oil) (3.2mm) | ASTM D149 | kV/mm | 18.1 | - |
Arc Resistance Arc Resistance/ASTM D495 | Arc Resistance, Tungsten (PLC) | ASTM D495 | PLC Code | 6 | 60≦D495<120 |
Tracking resistance Tracking resistance/UL 746A | CTI(Comparative Tracking Index)(UL,PLC) | UL 746A | PLC Code | 1 | 400≦CTI<600 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) (3.2mm) | SABIC method | % | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/SABIC method | Mold shrinkage (vertical direction) | SABIC method | % | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 3-4hr |
| Main Applications |
|---|
Indoor and outdoor electrical enclosures, Heating Ventilation/Air Conditioning (HVAC) applications, Solar/Photovoltaic (PV) interface candidates |
| Key Features |
|---|
Flame retardant, electrical performance, low moisture absorption, dimensional stability |