| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPE/PS |
| Product Name | NORYL |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Proportion | ASTM D792 | 1.13 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening point (Rate B/120) | ISO 306 | ℃ | 108 | - |
Vicat softening point (Rate B/50) | ASTM D1525 | ℃ | 101 | - | |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Af | HDT/Af(1.8 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Af | ℃ | 82 | - |
HDT/Bf(0.45 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Bf | ℃ | 95 | - | |
HDT (0.45 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 93 | - | |
HDT (0.45 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 98 | - | |
HDT (1.82 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 82 | - | |
HDT (1.82 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 86 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTM E831 | CTE(-40℃～+40℃)(flow direction) | ASTM E831 | x10^-5/℃ | 7.74 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ASTM E831 | CTE (-40℃～+40℃)(vertical direction) | ASTM E831 | x10^-5/℃ | 8.1 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point) (50mm/min) | ISO 527 | MPa | 66 | - |
Tensile strength (yield point) (Type I, 50 mm/min) | ASTM D638 | MPa | 62 | - | |
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) (50mm/min) | ISO 527 | MPa | 61 | - |
Tensile strength (break point) (Type I, 50 mm/min) | ASTEM D638 | MPa | 48 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (break point) (50mm/min) | ISO 527 | % | 4.5 | - |
Tensile elongation (break point) (Type I, 50 mm/min) | ASTM D638 | % | 18 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 2950 | - |
Tensile elasticity (50mm/min) | ASTM D638 | MPa | 2620 | - | |
Bending strength Bending strength/ISO 178 | Bending strength (yield point) (2mm/min) | ISO 178 | MPa | 107 | - |
Bending strength (yield point) (1.3mm/min, 50mm span) | ASTM D790 | MPa | 96 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending elasticity (2mm/min) | ISO 178 | MPa | 2600 | - |
Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 2410 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 10 | - |
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 213 | - | |
Tensile elongation Tensile elongation/ISO 527 | Tensile elongation (yield point) (50mm/min) | ISO 527 | % | 3.2 | - |
Tensile elongation (yield point) (Type I, 50 mm/min) | ASTM D638 | % | 3.6 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tracking resistance Tracking resistance/UL 746A | CTI(Comparative Tracking Index)(UL,PLC) | UL 746A | PLC Code | 2 | 250≦CTI<400 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) (3.2mm) | SABIC method | % | - | |
ＭＦＲ ＭＦＲ/ASTM D1238 | Melt flow rate (220℃/2.16kgf) | ASTM D1238 | g/10min | 14 | - |
Melt flow rate (260℃/3.8kgf) | ASTM D1238 | g/10min | 18 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 3-4hr |
| Key Features |
|---|
Flame retardant, high impact strength, dimensional stability, hydrolytic stability, low moisture absorption |