| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPE/PS |
| Product Name | NORYL |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density | ISO 1183 | g/cm^3 | 1.1 | - |
Proportion | ASTM D792 | 1.1 | - | ||
Water absorption Water absorption/ISO 62 | Water absorption (23℃/sat) | ISO 62 | % | 0.25 | - |
Water absorption rate (24 hours) | ASTM D570 | % | 0.07 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening point (Rate B/120) | ISO 306 | ℃ | 139 | - |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Af | HDT/Af(1.8 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Af | ℃ | 119 | - |
HDT (0.45 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 135 | - | |
HDT (1.82 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 123 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-2 | CTE(-40℃～+40℃)(flow direction) | ISO 11359-2 | x10^-5/℃ | 6.1 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ISO 11359-2 | CTE (-40℃～+40℃)(vertical direction) | ISO 11359-2 | x10^-5/℃ | 6.8 | - |
Linear expansion coefficient Linear expansion coefficient/TMA | CTE(-30℃～+30℃) | TMA | x10^-5/℃ | 7 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point) (50mm/min) | ISO 527 | MPa | 75 | - |
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) (50mm/min) | ISO 527 | MPa | 55 | - |
Tensile strength (break point) (Type I, 50 mm/min) | ASTEM D638 | MPa | 62 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (break point) (50mm/min) | ISO 527 | % | 8 | - |
Tensile elongation (break point) (Type I, 50 mm/min) | ASTM D638 | % | 15 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 2620 | - |
Tensile elasticity (50mm/min) | ASTM D638 | MPa | 2700 | - | |
Bending strength Bending strength/ISO 178 | Bending strength (yield point) (2mm/min) | ISO 178 | MPa | 109 | - |
Bending strength (yield point) (1.3mm/min, 50mm span) | ASTM D790 | MPa | 120 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending elasticity (2mm/min) | ISO 178 | MPa | 2530 | - |
Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 2800 | - | |
Charpy impact strength Charpy impact strength/ISO 179-1eA | Sharoppy strength 23℃ (V-notch Edgew 80*10*4 sp=62mm) | ISO 179-1eA | kJ/m^2 | 7 | - |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 8 | - |
Izod impact strength (notched, 80*10*4 -30℃) | ISO 180/1A | kJ/m^2 | 6 | - | |
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 100 | - | |
Tensile elongation Tensile elongation/ISO 527 | Tensile elongation (yield point) (50mm/min) | ISO 527 | % | 4.5 | - |
Tensile elongation (yield point) (Type I, 50 mm/min) | ASTM D638 | % | 5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Dielectric Strength Dielectric Strength/IEC 60243-1 | Dielectric breakdown strength (in oil) (3.2mm) | IEC 60243-1 | kV/mm | 49 | - |
Arc Resistance Arc Resistance/ASTM D495 | Arc Resistance, Tungsten (PLC) | ASTM D495 | PLC Code | 6 | 60≦D495<120 |
Tracking resistance Tracking resistance/UL 746A | CTI(Comparative Tracking Index)(UL,PLC) | UL 746A | PLC Code | 2 | 250≦CTI<400 |
CTI(Comparative Tracking Index) | IEC 60112 | V | 250 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294 | Mold shrinkage rate (flow direction) (24 hours) | ISO 294 | % | 0.5 | - |
Mold shrinkage rate (flow direction) (3.2mm) | SABIC method | % | - | ||
ＭＶＲ ＭＶＲ/ISO 1133 | Melt volume rate (280℃/5.0kgf) | ISO 1133 | cm3/10min | 12 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 3-4hr |
| Main Applications |
|---|
Charger, Adapter Housing |
| Key Features |
|---|
Flame retardant, dimensional stability, high heat resistance, low moisture absorption, electrical insulation |