| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPE/PS |
| Product Name | NORYL |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density | ISO 1183 | g/cm^3 | 1.11 | - |
Proportion | ASTM D792 | 1.11 | - | ||
Water absorption Water absorption/ISO 62 | Water absorption (23℃/sat) | ISO 62 | % | 0.18 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening point (Rate A/50) | ISO 306 | ℃ | 160 | - |
Vicat softening point (Rate B/50) | ISO 306 | ℃ | 145 | - | |
Vicat softening point (Rate B/120) | ISO 306 | ℃ | 155 | - | |
Vicat softening point (Rate B/50) | ASTM D1525 | ℃ | 155 | - | |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Ae | HDT/Ae(1.8 MPa Edgew 120*10*4 sp=100mm) | ISO 75/Ae | ℃ | 130 | - |
HDT/Be(0.45 MPa Edgew 120*10*4 sp=100mm) | ISO 75/Be | ℃ | 140 | - | |
HDT (1.82 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 135 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-2 | CTE(23℃～80℃)(flow direction) | ISO 11359-2 | x10^-5/℃ | 7 | - |
CTE(-40℃～+40℃)(flow direction) | ASTM E831 | x10^-5/℃ | 7.5 | - | |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ISO 11359-2 | CTE (23℃～80℃) (vertical direction) | ISO 11359-2 | x10^-5/℃ | 9 | - |
CTE (-40℃～+40℃)(vertical direction) | ASTM E831 | x10^-5/℃ | 7.5 | - | |
Thermal Conductivity Thermal Conductivity/ISO 8302 | Thermal Conductivity | ISO 8302 | W/m・℃ | 0.27 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point) (50mm/min) | ISO 527 | MPa | 70 | - |
Tensile strength (yield point) (Type I, 50 mm/min) | ASTM D638 | MPa | 70 | - | |
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) (50mm/min) | ISO 527 | MPa | 55 | - |
Tensile strength (break point) (Type I, 50 mm/min) | ASTEM D638 | MPa | 60 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (break point) (50mm/min) | ISO 527 | % | 10 | - |
Tensile elongation (break point) (Type I, 50 mm/min) | ASTM D638 | % | 7 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 2500 | - |
Tensile elasticity (5mm/min) | ASTM D638 | MPa | 2500 | - | |
Bending strength Bending strength/ISO 178 | Bending strength (yield point) (2mm/min) | ISO 178 | MPa | 110 | - |
Bending strength (yield point) (1.3mm/min, 50mm span) | ASTM D790 | MPa | 105 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending elasticity (2mm/min) | ISO 178 | MPa | 2400 | - |
Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 2550 | - | |
Charpy impact strength Charpy impact strength/ISO 179-1eA | Sharopy strength -30℃(V-notch Edgew 80*10*4 sp=62mm) | ISO 179-1eA | kJ/m^2 | 5 | - |
Sharoppy strength 23℃ (V-notch Edgew 80*10*4 sp=62mm) | ISO 179-1eA | kJ/m^2 | 14 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 13 | - |
Izod impact strength (notched, 80*10*4 -30℃) | ISO 180/1A | kJ/m^2 | 5 | - | |
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 330 | - | |
Izod impact strength (notched, -30℃) | ASTM D256 | J/m | 180 | - | |
Tensile elongation Tensile elongation/ISO 527 | Tensile elongation (yield point) (50mm/min) | ISO 527 | % | 4 | - |
Tensile elongation (yield point) (Type I, 50 mm/min) | ASTM D638 | % | 5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Volume resistivity Volume resistivity/IEC 60093 | Volume Resistivity | IEC 60093 | Ω・cm | NaN | - |
Surface resistance Surface resistance/IEC 60093 | Surface resistance | IEC 60093 | Ω | NaN | - |
Dielectric constant Dielectric constant/IEC 60250 | Dielectric constant, 1MHz | IEC 60250 | - | 2.7 | - |
Dielectric Strength Dielectric Strength/IEC 60243-1 | Dielectric breakdown strength (in oil) (0.8mm) | IEC 60243-1 | kV/mm | 33 | - |
Dielectric breakdown strength (in oil) (1.6mm) | IEC 60243-1 | kV/mm | 26 | - | |
Dielectric breakdown strength (in oil) (3.2mm) | IEC 60243-1 | kV/mm | 16 | - | |
Arc Resistance Arc Resistance/ASTM D495 | Arc Resistance, Tungsten (PLC) | ASTM D495 | PLC Code | 6 | 60≦D495<120 |
Tracking resistance Tracking resistance/UL 746A | CTI(Comparative Tracking Index)(UL,PLC) | UL 746A | PLC Code | 2 | 250≦CTI<400 |
CTI(Comparative Tracking Index) | IEC 60112 | V | 250 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) (3.2mm) | SABIC method | % | - | |
Mold shrinkage rate (flow direction) | SABIC method | % | - | ||
ＭＦＲ ＭＦＲ/ASTM D1238 | Melt flow rate (280℃/5.0kgf) | ASTM D1238 | g/10min | 3.5 | - |
ＭＶＲ ＭＶＲ/ISO 1133 | Melt volume rate (300℃/5.0kgf) | ISO 1133 | cm3/10min | 10 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 2-3hr |
| Main Applications |
|---|
Solar/Photovoltaic (PV) Junction Boxes, Outdoor Housings |
| Key Features |
|---|
Flame retardant, low temperature impact resistance, heat and humidity performance, low moisture absorption, dimensional stability |