| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPE/PS |
| Product Name | NORYL |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Proportion | ASTM D792 | 1.1 | - | |
Water absorption Water absorption/ASTM D570 | Balanced water absorption (23℃) | ASTM D570 | % | 0.06 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening point (Rate B/50) | ISO 306 | ℃ | 162 | - |
Vicat softening point (Rate B/120) | ISO 306 | ℃ | 164 | - | |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Ae | HDT/Ae(1.8 MPa Edgew 120*10*4 sp=100mm) | ISO 75/Ae | ℃ | 140 | - |
HDT/Be(0.45 MPa Edgew 120*10*4 sp=100mm) | ISO 75/Be | ℃ | 156 | - | |
HDT (0.45 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 155 | - | |
HDT (1.82 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 140 | - | |
HDT (1.82 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 145 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTM E831 | CTE(-40℃～+40℃)(flow direction) | ASTM E831 | x10^-5/℃ | 8 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ASTM E831 | CTE (-40℃～+40℃)(vertical direction) | ASTM E831 | x10^-5/℃ | 8 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point) | ISO 527 | MPa | 75 | - |
Tensile strength (yield point) (Type I, 50 mm/min) | ASTM D638 | MPa | 74 | - | |
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) | ISO 527 | MPa | 66 | - |
Tensile strength (break point) (Type I, 50 mm/min) | ASTEM D638 | MPa | 73 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (at break) | ISO 527 | % | 13 | - |
Tensile elongation (break point) (Type I, 50 mm/min) | ASTM D638 | % | 7.6 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 2220 | - |
Tensile elasticity (5mm/min) | ASTM D638 | MPa | 2380 | - | |
Bending strength Bending strength/ISO 178 | Bending strength | ISO 178 | MPa | 112 | - |
Bending strength (yield point) (1.3mm/min, 50mm span) | ASTM D790 | MPa | 110 | - | |
Bending strength (yield point) (2.6mm/min, 100mm span) | ASTM D790 | MPa | 110 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending Elasticity | ISO 178 | MPa | 2520 | - |
Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 2650 | - | |
Bending elasticity (2.6mm/min, 100mm span) | ASTM D790 | MPa | 2500 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 15 | - |
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 190 | - | |
Izod impact strength (notched, -30℃) | ASTM D256 | J/m | 55 | - | |
Tensile elongation Tensile elongation/ISO 527 | Tensile elongation (yield point) | ISO 527 | % | 5.2 | - |
Tensile elongation (yield point) (Type I, 50 mm/min) | ASTM D638 | % | 5.3 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Volume resistivity Volume resistivity/ASTM D257 | Volume Resistivity | ASTM D257 | Ω・cm | NaN | - |
Surface resistance Surface resistance/ASTM D257 | Surface resistance | ASTM D257 | Ω | NaN | - |
Dielectric constant Dielectric constant/ASTM D150 | Dielectric constant, 1MHz | ASTM D150 | - | 2.63 | - |
Dielectric constant, 50/60Hz | ASTM D150 | - | 2.68 | - | |
Dielectric Strength Dielectric Strength/ASTM D149 | Dielectric breakdown strength (in oil) (3.2mm) | ASTM D149 | kV/mm | 19.4 | - |
Arc Resistance Arc Resistance/ASTM D495 | Arc Resistance, Tungsten (PLC) | ASTM D495 | PLC Code | 6 | 60≦D495<120 |
Tracking resistance Tracking resistance/UL 746A | CTI(Comparative Tracking Index)(UL,PLC) | UL 746A | PLC Code | 3 | 175≦CTI<250 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) (3.2mm) | SABIC method | % | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/SABIC method | Mold shrinkage (vertical direction) | SABIC method | % | - | |
ＭＦＲ ＭＦＲ/ASTM D1238 | Melt flow rate (280℃/5.0kgf) | ASTM D1238 | g/10min | 7.4 | - |
ＭＶＲ ＭＶＲ/ISO 1133 | Melt volume rate (280℃/5.0kgf) | ISO 1133 | cm3/10min | 7 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 3-4hr |
| Main Applications |
|---|
Electrical Enclosures,Solar/Photovoltaic Junction Boxes |
| Key Features |
|---|
Flame retardant, low moisture absorption, dimensional stability, hydrolytic stability |