| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPE/PS |
| Product Name | NORYL |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Proportion | ASTM D792 | 1.38 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ASTM D1525 | Vicat softening point (Rate B/50) | ASTM D1525 | ℃ | 140 | - |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Af | HDT/Af(1.8 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Af | ℃ | 129 | - |
HDT (1.82 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 125 | - | |
Linear expansion coefficient Linear expansion coefficient/TMA | CTE(-30℃～+30℃) | TMA | x10^-5/℃ | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point) (5mm/min) | ISO 527 | MPa | 106 | - |
Tensile strength (yield point) (Type I, 5 mm/min) | ASTM D638 | MPa | 123 | - | |
Tensile breaking stress Tensile breaking stress/SABIC-Japan Method | Tensile strength (break point) (Type I, 10 mm/min) | SABIC-Japan Method | MPa | 115 | - |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (break point) (5mm/min) | ISO 527 | % | 1.3 | - |
Tensile elongation (break point) (Type I, 5 mm/min) | ASTM D638 | % | 1.5 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 10600 | - |
Tensile elasticity (5mm/min) | ASTM D638 | MPa | 11370 | - | |
Bending strength Bending strength/ISO 178 | Bending strength (yield point) (2mm/min) | ISO 178 | MPa | 160 | - |
Bending strength (yield point) (2.6mm/min, 100mm span) | ASTM D790 | MPa | 159 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending elasticity (2mm/min) | ISO 178 | MPa | 9130 | - |
Bending elasticity (2.6mm/min, 100mm span) | ASTM D790 | MPa | 8940 | - | |
Charpy impact strength Charpy impact strength/ISO 179-1eU | Sharopy strength 23℃ (Unnotch Edgew 80*10*4 sp=62mm) | ISO 179-1eU | kJ/m^2 | 20 | - |
Shalopy strength (notched, 23℃) | ISO 179/2C | kJ/m^2 | 4 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 5 | - |
Izod impact strength (unnotched, 80*10*4 +23℃) | ISO 180/1U | kJ/m^2 | 14 | - | |
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 68 | - | |
Izod impact strength (unnotched, 23℃) | ASTM D4812 | J/m | 331 | - | |
Tensile elongation Tensile elongation/SABIC Method | Tensile elongation (yield point) (Type I, 10 mm/min) | SABIC Method | % | 5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) | SABIC method | % | - | |
ＭＦＲ ＭＦＲ/ASTM D1238 | Melt flow rate (300℃/2.16kgf) | ASTM D1238 | g/10min | 11 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 3-4hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 35 | GF+mica |
| Main Applications |
|---|
Printer chassis |
| Key Features |
|---|
Flame retardant, dimensionally stable, low specific gravity, low warpage |