| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPE/PA |
| Product Name | NORYL GTX |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Density | ASTM D792 | g/cm^3 | 1.245 | - |
Proportion | ASTM D792 | 1.24 | - | ||
Water absorption Water absorption/ASTM D570 | Water absorption rate (24 hours) | ASTM D570 | % | 0.5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ASTM D1525 | Vicat softening point (Rate B/50) | ASTM D1525 | ℃ | 248 | - |
Deflection Temperature under Load Deflection Temperature under Load/ASTM D648 | HDT (0.45 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 254 | - |
HDT (1.82 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 232 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTM E831 | CTE(-20℃～+150℃)(flow direction) | ASTM E831 | x10^-5/℃ | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ASTM D638 | Tensile strength (yield point) (Type I, 5 mm/min) | ASTM D638 | MPa | 117 | - |
Tensile breaking stress Tensile breaking stress/ASTEM D638 | Tensile strength (break point) (Type I, 5mm/min) | ASTEM D638 | MPa | 117 | - |
Tensile strain at break Tensile strain at break/ASTM D638 | Tensile elongation (break point) (Type I, 5 mm/min) | ASTM D638 | % | 7 | - |
Bending strength Bending strength/ASTM D790 | Bending strength (yield point) (2.6mm/min, 100mm span) | ASTM D790 | MPa | 194 | - |
Flexural modulus Flexural modulus/ASTM D790 | Bending elasticity (2.6mm/min, 100mm span) | ASTM D790 | MPa | 5960 | - |
Izod impact strength Izod impact strength/ASTM D256 | Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 80 | - |
Izod impact strength (notched, -30℃) | ASTM D256 | J/m | 53 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) (3.2mm) | SABIC method | % | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/SABIC method | Mold shrinkage (vertical direction) (3.2mm) | SABIC method | % | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 3-4hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 20 | GF |
| Key Features |
|---|
Glass fiber reinforced, chemical resistance, high heat resistance |