| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPE/PA |
| Product Name | NORYL GTX |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density | ISO 1183 | g/cm^3 | 1.08 | - |
Proportion | ASTM D792 | 1.08 | - | ||
Water absorption Water absorption/ISO 62 | Water absorption (23℃/sat) | ISO 62 | % | 4.2 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening point (Rate B/50) | ISO 306 | ℃ | 195 | - |
Vicat softening point (Rate B/120) | ISO 306 | ℃ | 200 | - | |
Vicat softening point (Rate B/50) | ASTM D1525 | ℃ | 195 | - | |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Be | HDT/Be(0.45 MPa Edgew 120*10*4 sp=100mm) | ISO 75/Be | ℃ | 190 | - |
HDT (0.45 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 190 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-2 | CTE(23℃～60℃)(flow direction) | ISO 11359-2 | x10^-5/℃ | 9 | - |
CTE (-40℃～+60℃) (flow direction) | ASTM E831 | x10^-5/℃ | 8.5 | - | |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ISO 11359-2 | CTE (23℃～60℃) (vertical direction) | ISO 11359-2 | x10^-5/℃ | 9 | - |
CTE (-40℃～+40℃)(vertical direction) | ASTM E831 | x10^-5/℃ | 8.5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point) (50mm/min) | ISO 527 | MPa | 60 | - |
Tensile strength (yield point) (Type I, 50 mm/min) | ASTM D638 | MPa | 65 | - | |
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) (50mm/min) | ISO 527 | MPa | 55 | - |
Tensile strength (break point) (Type I, 50 mm/min) | ASTEM D638 | MPa | 60 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (break point) (50mm/min) | ISO 527 | % | 40 | - |
Tensile elongation (break point) (Type I, 50 mm/min) | ASTM D638 | % | 45 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 2300 | - |
Tensile elasticity (5mm/min) | ASTM D638 | MPa | 2350 | - | |
Bending strength Bending strength/ISO 178 | Bending strength (yield point) (2mm/min) | ISO 178 | MPa | 90 | - |
Bending strength (yield point) (1.3mm/min, 50mm span) | ASTM D790 | MPa | 95 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending elasticity (2mm/min) | ISO 178 | MPa | 2300 | - |
Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 2450 | - | |
Charpy impact strength Charpy impact strength/ISO 179-1eA | Sharopy strength -30℃(V-notch Edgew 80*10*4 sp=62mm) | ISO 179-1eA | kJ/m^2 | 15 | - |
Sharoppy strength 23℃ (V-notch Edgew 80*10*4 sp=62mm) | ISO 179-1eA | kJ/m^2 | 22 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 22 | - |
Izod impact strength (notched, 80*10*4 -30℃) | ISO 180/1A | kJ/m^2 | 15 | - | |
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 240 | - | |
Izod impact strength (notched, -30℃) | ASTM D256 | J/m | 180 | - | |
Tensile elongation Tensile elongation/ISO 527 | Tensile elongation (yield point) (50mm/min) | ISO 527 | % | 5 | - |
Tensile elongation (yield point) (Type I, 50 mm/min) | ASTM D638 | % | 5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) (3.2mm) | SABIC method | % | - | |
ＭＦＲ ＭＦＲ/ASTM D1238 | Melt flow rate (280℃/5.0kgf) | ASTM D1238 | g/10min | 16 | - |
ＭＶＲ ＭＶＲ/ISO 1133 | Melt volume rate (280℃/5.0kgf) | ISO 1133 | cm3/10min | 19 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 2-3hr |
| Main Applications |
|---|
Automotive applications, body panels, tank flaps, fenders, trunk lids, exterior trim |
| Key Features |
|---|
High heat resistance, high impact resistance, dimensional stability, electrostatic coating |