| Manufacturer | SABIC - SHPP Japan |
| Resin Name | PPE/PP |
| Product Name | NORYL PPX |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Proportion | ASTM D792 | 1.19 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ASTM D1525 | Vicat softening point (Rate B/50) | ASTM D1525 | ℃ | 162 | - |
Deflection Temperature under Load Deflection Temperature under Load/ASTM D648 | HDT (0.45 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 155 | - |
HDT (1.82 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 133 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTM E831 | CTE(-40℃～+40℃)(flow direction) | ASTM E831 | x10^-5/℃ | 1.44 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ASTM E831 | CTE (-40℃～+40℃)(vertical direction) | ASTM E831 | x10^-5/℃ | 7.74 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ASTM D638 | Tensile strength (yield point) (Type I, 5 mm/min) | ASTM D638 | MPa | 79 | - |
Tensile breaking stress Tensile breaking stress/ASTEM D638 | Tensile strength (break point) (Type I, 5mm/min) | ASTEM D638 | MPa | 79 | - |
Tensile strain at break Tensile strain at break/ASTM D638 | Tensile elongation (break point) (Type I, 5 mm/min) | ASTM D638 | % | 7.7 | - |
Bending strength Bending strength/ASTM D790 | Bending strength (yield point) (1.3mm/min, 50mm span) | ASTM D790 | MPa | 129 | - |
Flexural modulus Flexural modulus/ASTM D790 | Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 5550 | - |
Izod impact strength Izod impact strength/ASTM D256 | Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 165 | - |
Izod impact strength (notched, -30℃) | ASTM D256 | J/m | 101 | - | |
Izod impact strength (unnotched, 23℃) | ASTM D4812 | J/m | 827 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) (3.2mm) | SABIC method | % | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/SABIC method | Mold shrinkage (vertical direction) (3.2mm) | SABIC method | % | - | |
ＭＦＲ ＭＦＲ/ASTM D1238 | Melt flow rate (260℃/5.0kgf) | ASTM D1238 | g/10min | 2.6 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 2-4hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 30 | GF |
| Main Applications |
|---|
Exterior of hot water system, condensate housing, inside printer |
| Key Features |
|---|
Glass fiber reinforced, dimensionally stable, high rigidity |