| Manufacturer | SABIC - SHPP Japan |
| Resin Name | Polyetherimide |
| Product Name | ULTEM |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Proportion | ASTM D792 | 1.44 | - | |
Water absorption Water absorption/ASTM D570 | Water absorption rate (24 hours) | ASTM D570 | % | 0.06 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ASTM D648 | HDT (1.82 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 203 | - |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTM E831 | CTE(-40℃～+150℃)(flow direction) | ASTM E831 | x10^-5/℃ | 1.43 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ASTM E831 | CTE (-40℃～+150℃)(vertical direction) | ASTM E831 | x10^-5/℃ | 5.5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ASTEM D638 | Tensile strength (break point) (Type I, 5mm/min) | ASTEM D638 | MPa | 148 | - |
Tensile strain at break Tensile strain at break/ASTM D638 | Tensile elongation (break point) (Type I, 5 mm/min) | ASTM D638 | % | 1.8 | - |
Tensile Modulus Tensile Modulus/ASTM D638 | Tensile elasticity (5mm/min) | ASTM D638 | MPa | 10140 | - |
Bending strength Bending strength/ASTM D790 | Bending strength (yield point) (1.3mm/min, 50mm span) | ASTM D790 | MPa | 169 | - |
Flexural modulus Flexural modulus/ASTM D790 | Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 8090 | - |
Izod impact strength Izod impact strength/ASTM D256 | Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 76 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) | SABIC method | % | 0.3 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/SABIC method | Mold shrinkage (vertical direction) | SABIC method | % | 0.53 | - |
ＭＦＲ ＭＦＲ/ASTM D1238 | Melt flow rate (337℃/6.6kgf) | ASTM D1238 | g/10min | 15.4 | - |
ＭＶＲ ＭＶＲ/ISO 1133 | Melt volume rate (345℃/10.0kgf) | ISO 1133 | cm3/10min | 34 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 150 | 4-6hr |
| Main Applications |
|---|
Electronic equipment, displays, electrical components |
| Key Features |
|---|
High liquidity |