| Manufacturer | SABIC - SHPP Japan |
| Resin Name | Polyetherimide |
| Product Name | ULTEM |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Proportion | ASTM D792 | 1.67 | - | |
Water absorption Water absorption/ASTM D570 | Water absorption rate (24 hours) | ASTM D570 | % | 0.11 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ASTM D1525 | Vicat softening point (Rate B/50) | ASTM D1525 | ℃ | 233 | - |
Deflection Temperature under Load Deflection Temperature under Load/ASTM D648 | HDT (1.82 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 212 | - |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTM E831 | CTE(-40℃～+40℃)(flow direction) | ASTM E831 | x10^-5/℃ | 1.62 | - |
CTE(-20℃～+150℃)(flow direction) | ASTM E831 | x10^-5/℃ | 1.62 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ASTEM D638 | Tensile strength (break point) (Type I, 5mm/min) | ASTEM D638 | MPa | 82 | - |
Tensile strain at break Tensile strain at break/ASTM D638 | Tensile elongation (break point) (Type I, 5 mm/min) | ASTM D638 | % | 1.2 | - |
Bending strength Bending strength/ASTM D790 | Bending strength (break point) (2.6mm/min, 100mm span) | ASTM D790 | MPa | 137 | - |
Bending strength (yield point) (2.6mm/min, 100mm span) | ASTM D790 | MPa | 113 | - | |
Flexural modulus Flexural modulus/ASTM D790 | Bending elasticity (2.6mm/min, 100mm span) | ASTM D790 | MPa | 8820 | - |
Izod impact strength Izod impact strength/ASTM D256 | Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 64 | - |
Izod impact strength (reverse notched, 3.2 mm) | ASTM D256 | J/m | 170 | - | |
Izod impact strength (unnotched, 23℃) | ASTM D4812 | J/m | 160 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tracking resistance Tracking resistance/UL 746A | CTI(Comparative Tracking Index)(UL,PLC) | UL 746A | PLC Code | 4 | 100≦CTI<175 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) (3.2mm) | SABIC method | % | - | |
ＭＦＲ ＭＦＲ/ASTM D1238 | Melt flow rate (337℃/6.6kgf) | ASTM D1238 | g/10min | 3.1 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 135 | 4-6hr |
| Main Applications |
|---|
Electronic equipment, displays, electrical components |
| Key Features |
|---|
Glass fiber reinforced |