| Manufacturer | SABIC - SHPP Japan |
| Resin Name | Polyetherimide |
| Product Name | EXTEM |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density | ISO 1183 | g/cm^3 | 1.3 | - |
Proportion | ASTM D792 | 1.3 | - | ||
Water absorption Water absorption/ISO 62 | Water absorption (23℃/sat) | ISO 62 | % | 1.75 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening point (Rate B/50) | ISO 306 | ℃ | 242 | - |
Vicat softening point (Rate B/120) | ISO 306 | ℃ | 238 | - | |
Vicat softening point (Rate B/50) | ASTM D1525 | ℃ | 242 | - | |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Af | HDT/Af(1.8 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Af | ℃ | 228 | - |
HDT (0.45 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 237 | - | |
HDT (1.82 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 217 | - | |
HDT (1.82 MPa, 6.4 mm, no annealing) | ASTM D648 | ℃ | 230 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-2 | CTE(23℃～150℃)(flow direction) | ISO 11359-2 | x10^-5/℃ | 5 | - |
CTE(-40℃～+150℃)(flow direction) | ASTM E831 | x10^-5/℃ | 5 | - | |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ISO 11359-2 | CTE (23℃～150℃) (vertical direction) | ISO 11359-2 | x10^-5/℃ | 5 | - |
CTE (-20℃～+150℃)(vertical direction) | ASTM E831 | x10^-5/℃ | 5 | - | |
Thermal Conductivity Thermal Conductivity/ASTM E1530 | Thermal Conductivity | ASTM E1530 | W/m・℃ | 0.22 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point) (5mm/min) | ISO 527 | MPa | 95 | - |
Tensile strength (yield point) (Type I, 5 mm/min) | ASTM D638 | MPa | 96 | - | |
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) (5mm/min) | ISO 527 | MPa | 78 | - |
Tensile strength (break point) (Type I, 5mm/min) | ASTEM D638 | MPa | 96 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (break point) (5mm/min) | ISO 527 | % | 16.8 | - |
Tensile elongation (break point) (Type I, 5 mm/min) | ASTM D638 | % | 50 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 3110 | - |
Tensile elasticity (5mm/min) | ASTM D638 | MPa | 3510 | - | |
Bending strength Bending strength/ISO 178 | Bending strength (yield point) (2mm/min) | ISO 178 | MPa | 123 | - |
Flexural strength (break point) (1.3mm/min, 50mm span) | ASTM D790 | MPa | 159 | - | |
Bending strength (yield point) (2.6mm/min, 100mm span) | ASTM D790 | MPa | 155 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending elasticity (2mm/min) | ISO 178 | MPa | 2080 | - |
Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 3170 | - | |
Charpy impact strength Charpy impact strength/ISO 179-1eU | Sharopy strength -30℃(Unnotch Edgew 80*10*4 sp=62mm) | ISO 179-1eU | kJ/m^2 | NB | |
Sharopy strength 23℃ (Unnotch Edgew 80*10*4 sp=62mm) | ISO 179-1eU | kJ/m^2 | NB | ||
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 4 | - |
Izod impact strength (notched, 80*10*4 -30℃) | ISO 180/1A | kJ/m^2 | 5 | - | |
Izod impact strength (unnotched, 80*10*4 +23℃) | ISO 180/1U | kJ/m^2 | NB | ||
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 69 | - | |
Izod impact strength (notched, -30℃) | ASTM D256 | J/m | 74 | - | |
Izod impact strength (unnotched, 23℃) | ASTM D4812 | J/m | NB | ||
Tensile elongation Tensile elongation/ISO 527 | Tensile elongation (yield point) (5mm/min) | ISO 527 | % | 8.5 | - |
Tensile elongation (yield point) (Type I, 5mm/min) | ASTM D638 | % | 6 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Dielectric constant Dielectric constant/ASTM D150 | Specific permittivity, 1kHz | ASTM D150 | - | 3.41 | - |
Dielectric constant, 100Hz | ASTM D150 | - | 3.41 | - | |
Dielectric Strength Dielectric Strength/ASTM D149 | Dielectric breakdown strength (in oil) (3.2mm) | ASTM D149 | kV/mm | 17 | - |
Tracking resistance Tracking resistance/UL 746A | CTI(Comparative Tracking Index)(UL,PLC) | UL 746A | PLC Code | 3 | 175≦CTI<250 |
CTI(Comparative Tracking Index) | IEC 60112 | V | 175 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) (3.2mm) | SABIC method | % | - | |
Mold shrinkage rate (flow direction) | SABIC method | % | - | ||
Mold shrinkage rate TD Mold shrinkage rate TD/SABIC method | Mold shrinkage (vertical direction) (3.2mm) | SABIC method | % | - | |
ＭＦＲ ＭＦＲ/ASTM D1238 | Melt flow rate (367℃/6.6kgf) | ASTM D1238 | g/10min | 15.5 | - |
ＭＶＲ ＭＶＲ/ISO 1133 | Melt volume rate (360℃/5.0kgf) | ISO 1133 | cm3/10min | 8 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 150 | 4-6hr |
| Key Features |
|---|
Flame retardant, high heat resistance |