| Manufacturer | SABIC - SHPP Japan |
| Resin Name | Polyetherimide |
| Product Name | ULTEM |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density | ISO 1183 | g/cm^3 | 1.34 | - |
Proportion | ASTM D792 | 1.34 | - | ||
Water absorption Water absorption/ISO 62 | Water absorption (23℃/sat) | ISO 62 | % | 0.39 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening point (Rate B/120) | ISO 306 | ℃ | 173 | - |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75/Af | HDT/Af(1.8 MPa Flatw 80*10*4 sp=64mm) | ISO 75/Af | ℃ | 152 | - |
HDT (1.82 MPa, 3.2 mm, no annealing) | ASTM D648 | ℃ | 153 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point) (5mm/min) | ISO 527 | MPa | 88 | - |
Tensile strength (yield point) (Type I, 5 mm/min) | ASTM D638 | MPa | 84 | - | |
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point) (5mm/min) | ISO 527 | MPa | 71 | - |
Tensile strength (break point) (Type I, 5mm/min) | ASTEM D638 | MPa | 74 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation (break point) (5mm/min) | ISO 527 | % | 50 | - |
Tensile elongation (break point) (Type I, 5 mm/min) | ASTM D638 | % | 72 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile elasticity (1mm/min) | ISO 527 | MPa | 3050 | - |
Tensile elasticity (5mm/min) | ASTM D638 | MPa | 3440 | - | |
Bending strength Bending strength/ISO 178 | Bending strength (yield point) (2mm/min) | ISO 178 | MPa | 90 | - |
Bending strength (yield point) (1.3mm/min, 50mm span) | ASTM D790 | MPa | 138 | - | |
Flexural modulus Flexural modulus/ISO 178 | Bending elasticity (2mm/min) | ISO 178 | MPa | 2750 | - |
Bending elasticity (1.3mm/min, 50mm span) | ASTM D790 | MPa | 2920 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength (notched, 80*10*4 +23℃) | ISO 180/1A | kJ/m^2 | 13 | - |
Izod impact strength (notched, 23℃) | ASTM D256 | J/m | 115 | - | |
Tensile elongation Tensile elongation/ISO 527 | Tensile elongation (yield point) (5mm/min) | ISO 527 | % | 6.7 | - |
Tensile elongation (yield point) (Type I, 5mm/min) | ASTM D638 | % | 7 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/SABIC method | Mold shrinkage rate (flow direction) (3.2mm) | SABIC method | % | - | |
ＭＦＲ ＭＦＲ/ASTM D1238 | Melt flow rate (295℃/6.6kgf) | ASTM D1238 | g/10min | 8.9 | - |
ＭＶＲ ＭＶＲ/ISO 1133 | Melt volume rate (340℃/5.0kgf) | ISO 1133 | cm3/10min | 40 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying temperature | ℃ | 135 | 4-6hr |
| Main Applications |
|---|
Railway and aircraft interiors |
| Key Features |
|---|
High liquidity |