Density (23℃)

ISO 1183

g/cm^3

-

Bulk density (23℃)

ISO 60

g/cm3

0.7 or less

Water absorption (at equilibrium) (23℃, 50%RH)

ISO 62

%

1.4 or less

Water absorption (when saturated) (23℃ water)

ISO 62

%

4 or less

Vicat softening temperature (50N, 120℃/h)

ISO 306

℃

Lower limit

Deflection temperature under load (1.80MPa)

ISO 75-1,-2

℃

Under 250

Deflection temperature under load (0.45MPa)

ISO 75-1,-2

℃

Under 250

Melting point (10℃/min)

ISO 11357-1,-3

℃

-

Tensile breaking strength (5mm/min)

ISO 527-1,-2

MPa

220

Tensile elongation at break (5mm/min)

ISO 527-1,-2

%

-

Tensile modulus (1mm/min)

ISO 527-1,-2

MPa

-

Bending strength (2mm/min)

ISO 178-A

MPa

-

Flexural modulus (2mm/min)

ISO 178-A

MPa

-

Charpy impact strength (23℃)

ISO 179-1eU

kJ/m^2

-

Charpy impact strength (-30℃)

ISO 179-1eU

kJ/m^2

-

Charpy impact strength (notched, 23℃)

ISO 179-1eA

kJ/m^2

-

Charpy impact strength (notched, -30℃)

ISO 179-1eA

kJ/m^2

-

Izod impact strength (notched, 23℃)

ISO 180-1A

KJ/m^2

-

Izod impact strength (notched, -30℃)

ISO 180-1A

KJ/m^2

-

Bending strain at bending strength (2mm/min)

ISO 178-A

%

-

Mold shrinkage (parallel direction, 150×105×3, 300℃/MT80℃, 400bar)

ISO 2577

%

-

Mold shrinkage (vertical direction, 150 x 105 x 3, 300℃/MT80℃, 400bar)

ISO 2577

%

-

Resin temperature

℃

-

Mold Temperature

℃

-

Drying conditions

℃

2-6hr

Filler Content

%

GF