| Manufacturer | LANXESS K.K. |
| Resin Name | PA6 |
| Product Name | Durethan |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Melting point Melting point/ISO 11357-1,-3 | Melting point (10℃/min) | ISO 11357-1,-3 | ℃ | 219 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile strain at break Tensile strain at break/ISO 527-1,-2 | Nominal tensile strain at break (50mm/min) | ISO 527-1,-2 | % | 165 | - |
Tensile Modulus Tensile Modulus/ISO 527-1,-2 | Tensile modulus (1mm/min) | ISO 527-1,-2 | MPa | 430 | - |
Bending strength Bending strength/ISO 178-A | Bending strength (2mm/min) | ISO 178-A | MPa | 21 | - |
Bending stress at 3.5% displacement (2mm/min) | ISO 178-A | MPa | 14 | - | |
Flexural modulus Flexural modulus/ISO 178-A | Flexural modulus (2mm/min) | ISO 178-A | MPa | 470 | - |
Charpy impact strength Charpy impact strength/ISO 179-1eU | Charpy impact strength (23℃) | ISO 179-1eU | kJ/m^2 | NB | |
Charpy impact strength (-30℃) | ISO 179-1eU | kJ/m^2 | NB | ||
Charpy impact strength (notched, 23℃) | ISO 179-1eA | kJ/m^2 | 130 | - | |
Charpy impact strength (notched, -30℃) | ISO 179-1eA | kJ/m^2 | 25 | - | |
Izod impact strength Izod impact strength/ISO 180-1U | Izod impact strength (23℃) | ISO 180-1U | kJ/m^2 | NB | |
Izod impact strength (-30℃) | ISO 180-1U | KJ/m^2 | NB | ||
Izod impact strength (notched, 23℃) | ISO 180-1A | KJ/m^2 | 105 | - | |
Izod impact strength (notched, -30℃) | ISO 180-1A | KJ/m^2 | 25 | - | |
Yield Strain Yield Strain/ISO 178-A | Bending strain at bending strength (2mm/min) | ISO 178-A | % | 9 | - |
| Key Features |
|---|
Unreinforced, Blow Molded, Impact Improved, Heat Stable |