Public Beta
Public Beta
| Manufacturer | LANXESS K.K. |
| Resin Name | PA6 |
| Product Name | Durethan |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (23℃) | ISO 1183 | g/cm^3 | 1.03 | - |
Water absorption Water absorption/ISO 62 | Water absorption (at equilibrium) (23℃, 50%RH) | ISO 62 | % | 1.9 | - |
Water absorption (when saturated) (23℃ water) | ISO 62 | % | 8.1 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1,-2 | Deflection temperature under load (1.80MPa) | ISO 75-1,-2 | ℃ | 48 | - |
Deflection temperature under load (0.45MPa) | ISO 75-1,-2 | ℃ | 53 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-1,-2 | Linear expansion coefficient (parallel direction) (23℃-55℃) | ISO 11359-1,-2 | x10^-5/℃ | 20 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ISO 11359-1,-2 | Linear expansion coefficient (vertical direction) (23℃-55℃) | ISO 11359-1,-2 | x10^-5/℃ | 20 | - |
Melting point Melting point/ISO 11357-1,-3 | Melting point (10℃/min) | ISO 11357-1,-3 | ℃ | 212 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527-1,-2 | Tensile yield strength (50mm/min) | ISO 527-1,-2 | MPa | 28 | - |
Tensile Modulus Tensile Modulus/ISO 527-1,-2 | Tensile modulus (1mm/min) | ISO 527-1,-2 | MPa | 980 | - |
Bending strength Bending strength/ISO 178-A | Bending strength (2mm/min) | ISO 178-A | MPa | 35 | - |
Bending stress at 3.5% displacement (2mm/min) | ISO 178-A | MPa | 30 | - | |
Flexural modulus Flexural modulus/ISO 178-A | Flexural modulus (2mm/min) | ISO 178-A | MPa | 980 | - |
Charpy impact strength Charpy impact strength/ISO 179-1eU | Charpy impact strength (23℃) | ISO 179-1eU | kJ/m^2 | NB | |
Charpy impact strength (-30℃) | ISO 179-1eU | kJ/m^2 | NB | ||
Charpy impact strength (notched, 23℃) | ISO 179-1eA | kJ/m^2 | 105 | - | |
Charpy impact strength (notched, -30℃) | ISO 179-1eA | kJ/m^2 | 75 | - | |
Izod impact strength Izod impact strength/ISO 180-1U | Izod impact strength (23℃) | ISO 180-1U | kJ/m^2 | NB | |
Izod impact strength (-30℃) | ISO 180-1U | KJ/m^2 | NB | ||
Izod impact strength (notched, 23℃) | ISO 180-1A | KJ/m^2 | 90 | - | |
Izod impact strength (notched, -30℃) | ISO 180-1A | KJ/m^2 | 70 | - | |
Tensile elongation Tensile elongation/ISO 527-1,-2 | Tensile yield elongation (50mm/min) | ISO 527-1,-2 | % | 6.5 | - |
Yield Strain Yield Strain/ISO 178-A | Bending strain at bending strength (2mm/min) | ISO 178-A | % | 6.1 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 80 | 2-6hr |
| Key Features |
|---|
Copolymer, Unreinforced, Blow Molding, Heat Stable, Impact Improved, Heat Stable |