| Manufacturer | LANXESS K.K. |
| Resin Name | PA6 |
| Product Name | Durethan |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (23℃) | ISO 1183 | g/cm^3 | 1.63 | - |
Bulk density (23℃) | ISO 60 | g/cm^3 | 0.88 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening temperature (50N, 120℃/h) | ISO 306 | ℃ | 200 | - |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1,-2 | Deflection temperature under load (1.80MPa) | ISO 75-1,-2 | ℃ | 185 | - |
Deflection temperature under load (0.45MPa) | ISO 75-1,-2 | ℃ | 210 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-1,-2 | Linear expansion coefficient (parallel direction) (23℃-55℃) | ISO 11359-1,-2 | x10^-5/℃ | 3 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ISO 11359-1,-2 | Linear expansion coefficient (vertical direction) (23℃-55℃) | ISO 11359-1,-2 | x10^-5/℃ | 9 | - |
Melting point Melting point/ISO 11357-1,-3 | Melting point (10℃/min) | ISO 11357-1,-3 | ℃ | 222 | - |
Flammability Flammability/UL 94 | Combustion Test | UL 94 | NaN | 0.75mm | |
Combustion Test | UL 94 | NaN | 1.5mm |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO 527-1,-2 | Tensile breaking strength (5mm/min) | ISO 527-1,-2 | MPa | 105 | - |
Tensile strain at break Tensile strain at break/ISO 527-1,-2 | Tensile elongation at break (5mm/min) | ISO 527-1,-2 | % | 2.7 | - |
Tensile Modulus Tensile Modulus/ISO 527-1,-2 | Tensile modulus (1mm/min) | ISO 527-1,-2 | MPa | 7500 | - |
Bending strength Bending strength/ISO 178-A | Bending strength (2mm/min) | ISO 178-A | MPa | 175 | - |
Flexural modulus Flexural modulus/ISO 178-A | Flexural modulus (2mm/min) | ISO 178-A | MPa | 7300 | - |
Charpy impact strength Charpy impact strength/ISO 179-1eU | Charpy impact strength (23℃) | ISO 179-1eU | kJ/m^2 | 40 | - |
Charpy impact strength (-30℃) | ISO 179-1eU | kJ/m^2 | 30 | - | |
Charpy impact strength (notched, 23℃) | ISO 179-1eA | kJ/m^2 | 10 | - | |
Charpy impact strength (notched, -30℃) | ISO 179-1eA | kJ/m^2 | 10 | - | |
Izod impact strength Izod impact strength/ISO 180-1U | Izod impact strength (23℃) | ISO 180-1U | kJ/m^2 | 40 | - |
Izod impact strength (-30℃) | ISO 180-1U | KJ/m^2 | 30 | - | |
Izod impact strength (notched, 23℃) | ISO 180-1A | KJ/m^2 | 10 | < Less than | |
Izod impact strength (notched, -30℃) | ISO 180-1A | KJ/m^2 | 10 | < Less than | |
Yield Strain Yield Strain/ISO 178-A | Bending strain at bending strength (2mm/min) | ISO 178-A | % | 2.8 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Dielectric Strength Dielectric Strength/IEC 60243-1 | Dielectric breakdown strength (1mm) | IEC 60243-1 | kV/mm | 33 | - |
Tracking resistance Tracking resistance/UL 746A | Comparative Tracking Index CTI (Solution A) | UL 746A | PLC | 1 | 400≦CTI<600 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294-4 | Mold shrinkage (parallel direction, 60x60x2, 280℃/MT80℃, 600bar) | ISO 294-4 | % | 0.4 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 294-4 | Mold shrinkage (vertical direction, 60x60x2, 280℃/MT80℃, 600bar) | ISO 294-4 | % | 0.7 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 80 | 2-6hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 30 | GF+GB |
| Key Features |
|---|
Injection molding grade, flame retardant grade, low warpage, excellent appearance, heat stability |