| Manufacturer | LANXESS K.K. |
| Resin Name | PA6 |
| Product Name | Durethan |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (23℃) | ISO 1183 | g/cm^3 | 1.57 | - |
Water absorption Water absorption/ISO 62 | Water absorption (at equilibrium) (23℃, 50%RH) | ISO 62 | % | 1.5 | - |
Water absorption (when saturated) (23℃ water) | ISO 62 | % | 5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening temperature (50N, 120℃/h) | ISO 306 | ℃ | 215 | - |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1,-2 | Deflection temperature under load (1.80MPa) | ISO 75-1,-2 | ℃ | 210 | - |
Deflection temperature under load (0.45MPa) | ISO 75-1,-2 | ℃ | 220 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-1,-2 | Linear expansion coefficient (parallel direction) (23℃-55℃) | ISO 11359-1,-2 | x10^-5/℃ | 1.5 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ISO 11359-1,-2 | Linear expansion coefficient (vertical direction) (23℃-55℃) | ISO 11359-1,-2 | x10^-5/℃ | 8 | - |
Melting point Melting point/ISO 11357-1,-3 | Melting point (10℃/min) | ISO 11357-1,-3 | ℃ | 220 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO 527-1,-2 | Tensile breaking strength (5mm/min) | ISO 527-1,-2 | MPa | 220 | - |
Tensile breaking strength (5mm/min, 120℃) | ISO 527-1,-2 | MPa | 105 | - | |
Tensile strain at break Tensile strain at break/ISO 527-1,-2 | Tensile elongation at break (5mm/min) | ISO 527-1,-2 | % | 3 | - |
Tensile elongation at break (5mm/min, 120℃) | ISO 527-1,-2 | % | 7.5 | - | |
Tensile Modulus Tensile Modulus/ISO 527-1,-2 | Tensile modulus (1mm/min) | ISO 527-1,-2 | MPa | 16300 | - |
Tensile modulus (1mm/min, 120℃) | ISO 527-1,-2 | MPa | 6500 | - | |
Bending strength Bending strength/ISO 178-A | Bending strength (2mm/min) | ISO 178-A | MPa | 360 | - |
Flexural modulus Flexural modulus/ISO 178-A | Flexural modulus (2mm/min) | ISO 178-A | MPa | 15100 | - |
Charpy impact strength Charpy impact strength/ISO 179-1eU | Charpy impact strength (23℃) | ISO 179-1eU | kJ/m^2 | 100 | - |
Charpy impact strength (-30℃) | ISO 179-1eU | kJ/m^2 | 100 | - | |
Charpy impact strength (notched, 23℃) | ISO 179-1eA | kJ/m^2 | 20 | - | |
Charpy impact strength (notched, -30℃) | ISO 179-1eA | kJ/m^2 | 17 | - | |
Izod impact strength Izod impact strength/ISO 180-1U | Izod impact strength (23℃) | ISO 180-1U | kJ/m^2 | 90 | - |
Izod impact strength (-30℃) | ISO 180-1U | KJ/m^2 | 90 | - | |
Izod impact strength (notched, 23℃) | ISO 180-1A | KJ/m^2 | 20 | - | |
Izod impact strength (notched, -30℃) | ISO 180-1A | KJ/m^2 | 15 | - | |
Yield Strain Yield Strain/ISO 178-A | Bending strain at bending strength (2mm/min) | ISO 178-A | % | 3.3 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294-4 | Mold shrinkage rate (parallel direction, 60 x 60 x 2) | ISO 294-4 | % | 0.25 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 294-4 | Molding shrinkage rate (vertical direction, 60 x 60 x 2) | ISO 294-4 | % | 0.7 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 80 | 2-6hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 50 | GF |
| Key Features |
|---|
Injection molding grade, heat stability, improved fatigue resistance |