Density (23℃)

ISO 1183

g/cm^3

-

Bulk density (23℃)

ISO 60

g/cm^3

-

Water absorption (at equilibrium) (23℃, 50%RH)

ISO 62

%

-

Water absorption (when saturated) (23℃ water)

ISO 62

%

-

Deflection temperature under load (1.80MPa)

ISO 75-1,-2

℃

-

Deflection temperature under load (0.45MPa)

ISO 75-1,-2

℃

-

Linear expansion coefficient (parallel direction) (23℃-55℃)

ISO 11359-1,-2

x10^-5/℃

-

Linear expansion coefficient (vertical direction) (23℃-55℃)

ISO 11359-1,-2

x10^-5/℃

-

Melting point (10℃/min)

ISO 11357-1,-3

℃

-

Combustion Test

UL 94

0.75mm

Combustion Test

UL 94

1.5mm

Tensile breaking strength (5mm/min)

ISO 527-1,-2

MPa

-

Tensile elongation at break (5mm/min)

ISO 527-1,-2

%

-

Tensile modulus (1mm/min)

ISO 527-1,-2

MPa

-

Bending strength (2mm/min)

ISO 178-A

MPa

-

Bending stress at 3.5% displacement (2mm/min)

ISO 178-A

MPa

-

Flexural modulus (2mm/min)

ISO 178-A

MPa

-

Charpy impact strength (23℃)

ISO 179-1eU

kJ/m^2

-

Charpy impact strength (-30℃)

ISO 179-1eU

kJ/m^2

-

Charpy impact strength (notched, 23℃)

ISO 179-1eA

kJ/m^2

-

Charpy impact strength (notched, -30℃)

ISO 179-1eA

kJ/m^2

-

Izod impact strength (23℃)

ISO 180-1U

kJ/m^2

-

Izod impact strength (-30℃)

ISO 180-1U

KJ/m^2

-

Izod impact strength (notched, 23℃)

ISO 180-1A

KJ/m^2

< Less than

Izod impact strength (notched, -30℃)

ISO 180-1A

KJ/m^2

< Less than

Bending strain at bending strength (2mm/min)

ISO 178-A

%

-

Mold shrinkage (parallel direction, 150×105×3, 290℃/MT80℃, 500bar)

ISO 2577

%

-

Mold shrinkage (parallel direction, 60x60x2, 290℃/MT80℃, 600bar)

ISO 294-4

%

-

Mold shrinkage (vertical direction, 150×105×3, 290℃/MT80℃, 500bar)

ISO 2577

%

-

Mold shrinkage (vertical direction, 60x60x2, 290℃/MT80℃, 600bar)

ISO 294-4

%

-

Resin temperature

℃

-

Mold Temperature

℃

-

Drying conditions

℃

2-6hr

Filler Content

%

GF+MD