Public Beta
Public Beta
| Manufacturer | Fuwafon TPU (Nomura Trading) |
| Resin Name | TPU |
| Product Name | huafon Thermoplastic Polyurethane |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Proportion | ASTM D792 | g/cm3 | 1.12 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile strain at break Tensile strain at break/ASTM D412 | Breaking Elongation | ASTM D412 | % | 870 | - |
100% Modulus 100% Modulus/ASTM D412 | 100% tensile stress (100% tensile modulus) | ASTM D412 | MPa | 5.8 | - |
Tear strength Tear strength/ASTM D624 | Tear strength | ASTM D624 | kn/m | 103 | - |
Surface hardness Surface hardness/ASTM D2240 | Shore Hardness | ASTM D2240 | Shore A | 85 | - |
Tensile strength Tensile strength/ASTM D412 | Tensile strength | ASTM D412 | MPa | 30 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ | Shrinkage 115mm(L)×25mm(W)×2mm(T) Flow direction | % | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Recommended processing temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 90 | 3-5hrs |
| Color |
|---|
Colorless and transparent |
| Main Applications |
|---|
Extrusion Products |
| Key Features |
|---|
Ether-based TPU |