| Manufacturer | Sumitomo Chemical Co., Ltd. |
| Resin Name | LLDPE |
| Product Name | Excellen |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/JIS K6922-2 | Density | JIS K6922-2 | g/cm^3 | 0.895 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/JIS K7206 | Vicat softening point (test piece 150℃, 5min, 2.0MPa compression molding, preheating and cooling 5min) | JIS K7206 | ℃ | 54 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/Sumika method | Tensile breaking strength (test piece 150℃, 5min, 2.7MPa compression molding, preheating and cooling 5min) | Sumika method | MPa | 9 | - |
Tensile strain at break Tensile strain at break/Sumika method | Tensile elongation at break (test piece 150℃, 5min, 2.7MPa compression molding, preheating and cooling 5min) | Sumika method | % | 900 | - |
Flexural modulus Flexural modulus/ASTM D747-70 | Bending stiffness (test piece 150℃, 5min, 2.0MPa compression molding, preheating and cooling 5min) | ASTM D747-70 | MPa | 54 | - |
Surface hardness Surface hardness/JIS K7215 | Durometer hardness (test piece 150℃, 5min, 2.0MPa compression molding, preheating and cooling 5min) | JIS K7215 | D | 37 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
MFR MFR/JIS K6922-1 | Melt Flow Rate | JIS K6922-1 | g/10min | 10 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/Sumika method | Melting Temperature | Sumika method | ℃ | 114 | - |
| Main Applications |
|---|
PP Modification |