Density (density gradient tube method/pellet)

Mitsui Chemicals Method

g/cm^3

-

Water absorption (corner plate (1mm thick))

ISO 62

%

-

Vicat softening temperature (load: 10N, heating rate: 50℃/h/dumbbell piece (4mm))

ISO 306

℃

-

Deflection temperature under load (load: 0.45 MPa, heating rate 120°C/h/dumbbell piece (4 mm))

ISO 75

℃

-

Melting point (DSC method, heating rate: 10℃/min/pellet)

Mitsui Chemicals Method

℃

-

Yield stress (speed: 5mm/min/dumbbell piece (4mm))

ISO 527

MPa

-

Breaking stress (speed: 5mm/min/dumbbell piece (4mm))

ISO 527

MPa

-

Breaking stress (speed: 50mm/min/dumbbell piece (4mm))

ISO 527

MPa

-

Breaking elongation (speed: 5mm/min/dumbbell piece (4mm))

ISO 527

%

-

Breaking elongation (speed: 50 mm/min/dumbbell piece (4 mm))

ISO 527

%

-

Tensile modulus (speed: 2 mm/min/dumbbell piece (4 mm))

ISO 257

MPa

-

Bending strength (speed: 2mm/min/dumbbell piece (4mm))

ISO 178

MPa

-

Flexural modulus (speed: 2 mm/min/dumbbell piece (4 mm))

ISO 178

MPa

-

IZ impact test (with notch/dumbbell piece (4mm))

ISO 180 (Part 1 of Mitsui Chemicals)

kJ/m^2

-

IZ impact test (unnotched/dumbbell piece (4mm))

ISO 180 (Part 1 of Mitsui Chemicals)

kJ/m^2

-

Rockwell Hardness

ISO 2039

HRR Scale

-

Volume resistivity (square plate (2 mm thick))

IEC 60093

Ω・cm

>Lower limit

Dielectric constant (1MHz/square plate (2mm thick))

IEC 60250

-

Dielectric breakdown voltage (square plate (2 mm))

IEC 60243-1

kV/mm

-

Full haze (light source: D65/square plate (2mm thick))

ISO 14782

%

-

Total light transmittance (light source: D65/angle plate (2mm thick))

ISO 14782

%

-

Refractive index (light source: D-line/square plate (2 mm thick))

ISO 489

-

MFR (load: 5kg, test humidity: 260℃/pellet)

Mitsui Chemicals Method

g/10min

-