| Manufacturer | Mitsui Chemicals Fine Co., Ltd. |
| Resin Name | POK |
| Product Name | POKETONE |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Proportion | ASTM D792 | 1.24 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ASTM D648 | Deflection temperature under load (1.82MPa) | ASTM D648 | ℃ | 72 | - |
Melting point Melting point/ASTM D3418 | Melting point | ASTM D3418 | ℃ | 200 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Bending strength Bending strength/ASTM D790 | Bending strength | ASTM D790 | MPa | 45 | - |
Flexural modulus Flexural modulus/ASTM D790 | Flexural modulus | ASTM D790 | MPa | 1050 | - |
Charpy impact strength Charpy impact strength/ISO179/1eA | Charpy impact strength | ISO179/1eA | kJ/m2 | 9 | - |
Tensile Yield Stress Tensile Yield Stress/ASTM D638 | Tensile Yield Stress | ASTM D638 | MPa | 45 | - |
Tensile elongation at break Tensile elongation at break/ASTM D638 | Tensile elongation at break | ASTM D638 | % | 300 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
MFR MFR/ASTM D1238 | MFR(240℃×2.16Kgf) | ASTM D1238 | g/10min | 35 | - |
| Color |
|---|
Natural |
| Main Applications |
|---|
Monofilament |
| Key Features |
|---|
High flow, sliding properties, chemical resistance |