| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Resin Name | SPS |
| Product Name | XAREC |
| ISO Material Code | >(PS-HI+PS-ST)-GF25< |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density | ISO 1183 | g/cm^3 | 1.24 | - |
Water absorption Water absorption/ISO 62 | Water absorption (24h, 50%RH) | ISO 62 | % | 0.01 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75 A | Deflection temperature under load (1.8MPa) | ISO 75 A | ℃ | 135 | - |
Deflection temperature under load (0.45MPa) | ISO 75 B | ℃ | 140 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/TMA | Linear expansion coefficient, flow direction (MD), -30 to 30°C | TMA | ×10^-5/℃ | 2.4 | - |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/TMA | Linear expansion coefficient, transverse direction (TD), -30 to 30°C | TMA | ×10^-5/℃ | 3.9 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile Break Strength | ISO 527 | MPa | 125 | - |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile elongation at break | ISO 527 | % | 2.3 | - |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile Modulus | ISO 527 | MPa | 8200 | - |
Bending strength Bending strength/ISO 178 | Bending strength | ISO 178 | MPa | 195 | - |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus | ISO 178 | MPa | 7800 | - |
Charpy impact strength Charpy impact strength/ISO 179 | Charpy impact strength (notched at 23℃) | ISO 179 | kJ/m^2 | 14 | - |
Charpy impact strength (unnotched at 23℃) | ISO 179 | kJ/m^2 | 47 | - | |
Izod impact strength Izod impact strength/ISO 180 | Izod impact strength (notched at 23℃) | ISO 180 | kJ/m^2 | 13 | - |
Izod impact strength (unnotched at 23℃) | ISO 180 | kJ/m^2 | 43 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/Idemitsu Method | Mold shrinkage, machine direction (MD) | Idemitsu Method | % | Test piece: 80 x 80 x 2 mm injection molded product | |
Mold shrinkage rate TD Mold shrinkage rate TD/Idemitsu Method | Mold shrinkage, transverse direction (TD) | Idemitsu Method | % | Test piece: 80 x 80 x 2 mm injection molded product |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Cylinder Temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 80 | 3-5 hours |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Glass Fiber Content | % | 25 | - |
| Color |
|---|
Natural, black |
| Main Applications |
|---|
Housing facilities |
| Key Features |
|---|
Low specific gravity, impact resistance |